DIN 1725-1 Grade 3.2315 T5 Aluminum Tube – Technical Specifications

Properties

General

PropertyValueComment

Density

2.7 g/cm³

Typical for Wrought 6000 Series Aluminium

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Elastic modulus

70.0 GPa

Typical for Wrought 6000 Series Aluminium

Elongation

-75.0 °C

10.0 %

T5

DIN 1725-1

Seamless Tube

Transverse

-75.0 °C

14.0 %

T5

DIN 1725-1

Rod, Tube, Seamless Tube

20.0 °C

10.0 %

T5

DIN 1725-1

Seamless Tube

Transverse

20.0 °C

14.0 %

T5

DIN 1725-1

Rod, Tube, Seamless Tube

50.0 °C

10.0 %

T5

DIN 1725-1

Seamless Tube

Transverse

50.0 °C

14.0 %

T5

DIN 1725-1

Rod, Tube, Seamless Tube

100.0 °C

14.0 %

T5

DIN 1725-1

Rod, Tube, Seamless Tube

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Typical for Wrought 6000 Series Aluminium

Poisson's ratio

0.33 [-]

Typical for Wrought 6000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Typical for Wrought 6000 Series Aluminium

Tensile strength

-75.0 °C

275.0 MPa

T5

DIN 1725-1

Seamless Tube

-75.0 °C

275.0 MPa

T5

DIN 1725-1

Seamless Tube

Transverse

-75.0 °C

310.0 MPa

T5

DIN 1725-1

Rod, Tube, Seamless Tube

-75.0 °C

310.0 MPa

T5

DIN 1725-1

Seamless Tube

Transverse

20.0 °C

225.0 MPa

T5

DIN 1725-1

Tube

20.0 °C

250.0 MPa

T5

DIN 1725-1

Rod, Seamless Tube

20.0 °C

275.0 MPa

T5

DIN 1725-1

Seamless Tube

20.0 °C

275.0 MPa

T5

DIN 1725-1

Seamless Tube

Transverse

20.0 °C

310.0 MPa

T5

DIN 1725-1

Rod, Tube, Seamless Tube

20.0 °C

310.0 MPa

T5

DIN 1725-1

Seamless Tube

Transverse

20.0 °C

390.0 MPa

T5

DIN 1725-1

Rod

50.0 °C

190.0 MPa

T5

DIN 1725-1

Rod

50.0 °C

220.0 MPa

T5

DIN 1725-1

50.0 °C

250.0 MPa

T5

DIN 1725-1

Rod, Seamless Tube

50.0 °C

250.0 MPa

T5

DIN 1725-1

Seamless Tube

Transverse

50.0 °C

260.0 MPa

T5

DIN 1725-1

Rod

50.0 °C

280.0 MPa

T5

DIN 1725-1

Tube, Seamless Tube

50.0 °C

280.0 MPa

T5

DIN 1725-1

Seamless Tube

Transverse

50.0 °C

290.0 MPa

T5

DIN 1725-1

Rod, Tube

50.0 °C

300.0 MPa

T5

DIN 1725-1

Rod, Tube

100.0 °C

180.0 MPa

T5

DIN 1725-1

Rod

100.0 °C

210.0 MPa

T5

DIN 1725-1

Rod

100.0 °C

250.0 MPa

T5

DIN 1725-1

Rod, Seamless Tube

100.0 °C

280.0 MPa

T5

DIN 1725-1

Tube, Seamless Tube

100.0 °C

290.0 MPa

T5

DIN 1725-1

Rod, Tube

100.0 °C

335.0 MPa

T5

DIN 1725-1

Rod

Thermal

PropertyValueComment

Coefficient of thermal expansion

1.6e-05 - 2.4e-05 1/K

Typical for Wrought 6000 Series Aluminium

Melting point

555.0 - 655.0 °C

Typical for Wrought 6000 Series Aluminium

Specific heat capacity

887.0 - 963.0 J/(kg·K)

Typical for Wrought 6000 Series Aluminium

Thermal conductivity

170.0 - 220.0 W/(m·K)

Typical for Wrought 6000 Series Aluminium

Electrical

PropertyValueComment

Electrical conductivity

21000000.0 - 34000000.0 S/m

Typical for Wrought 6000 Series Aluminium

Electrical resistivity

2.9e-08 - 5e-08 Ω·m

Typical for Wrought 6000 Series Aluminium

Chemical properties

PropertyValueConditionRelated StandardsShape

Chromium

0.1 - 0.25 %

T5

DIN 1725-1

Rod, Tube

0.1 - 0.2 %

T5

DIN 1725-1

Seamless Tube

0.2 %

T5

DIN 1725-1

Seamless Tube

0.25 %

T5

DIN 1725-1

Rod

Copper

0.05

T5

DIN 1725-1

Tube

0.1

T5

DIN 1725-1

Rod, Tube, Seamless Tube

Iron

0.4

T5

DIN 1725-1

Seamless Tube, Tube

0.5

T5

DIN 1725-1

Rod, Tube

Magnesium

0.6 - 1.2 %

T5

DIN 1725-1

Rod, Tube, Seamless Tube

1.2 %

T5

DIN 1725-1

Seamless Tube

Manganese

0.4 - 1.0 %

T5

DIN 1725-1

Rod, Tube

0.4 - 0.8 %

T5

DIN 1725-1

Seamless Tube

0.8 %

T5

DIN 1725-1

Seamless Tube

Silicon

0.7 - 1.3 %

T5

DIN 1725-1

Rod, Tube, Seamless Tube

0.75 - 1.3 %

T5

DIN 1725-1

Tube

1.3 %

T5

DIN 1725-1

Seamless Tube

Titanium

0.1

T5

DIN 1725-1

Rod, Tube, Seamless Tube

Zinc

0.2

T5

DIN 1725-1

Rod, Tube, Seamless Tube

Technological properties

Property
Workability

Excellent workability.


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1725-1 Grade 3.4415 – High-Performance Al–Zn Alloy for Corrosion Protection
    2. DIN 1725-1 Grade 3.4365 T5 – High‑Strength 7075 Aluminum Alloy for Aerospace
    3. DIN 1725‑1 Grade 3.4365 O – Premium High‑Strength Aluminum Alloy for Aerospace
    4. DIN 1725-1 Grade 3.4335 T5 Aluminum Alloy – High-Performance Wrought Grade
    5. DIN 1725-1 Grade 3.3211 T8 Alloy: Superior Corrosion Resistance & Finish
    6. DIN 1725-1 Grade 3.0615 T8: High-Performance Free-Cutting Alloy
    7. DIN 1725-1 Grade 3.1255 T8 Aluminum Alloy – High Strength & Precision Machining
    8. DIN 1725-1 Grade 3.0615 T3 – High‑Performance AlMgSiPb Free‑Cutting Alloy
    9. DIN 1725-1 Grade 3.2315 T3 – High-Strength AlMgSi Alloy for Precision Applications
    10. DIN 1725-1 Grade 3.2315 T8: Premium AlMgSi Alloy with High Strength and Versatility