DIN 1725‑1 Grade 3.3537 O Aluminium Sheet – Key Properties & Standards
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Wrought 5000 Series Aluminium |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | ||||
Elongation | 20.0 °C | 18.0 | O | DIN 1725-1 | Sheet, Strip | Transverse |
20.0 °C | 18.0 % | O | DIN 1725-1 | Sheet, Strip | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 220.0 MPa | O | DIN 1725-1 | Sheet, Strip | Transverse |
20.0 °C | 220.0 MPa | O | DIN 1725-1 | Sheet, Strip |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.05 - 0.2 % | O | DIN 1725-1 | Sheet, Strip |
Copper | 0.1 | O | DIN 1725-1 | Sheet, Strip |
Iron | 0.4 | O | DIN 1725-1 | Sheet, Strip |
Magnesium | 2.4 - 3.0 % | O | DIN 1725-1 | Sheet, Strip |
Manganese | 0.5 - 1.0 % | O | DIN 1725-1 | Sheet, Strip |
Silicon | 0.25 | O | DIN 1725-1 | Sheet, Strip |
Titanium | 0.2 | O | DIN 1725-1 | Sheet, Strip |
Zinc | 0.25 | O | DIN 1725-1 | Sheet, Strip |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- DIN 1725-1 Grade 3.4415 – High-Performance Al–Zn Alloy for Corrosion Protection
- DIN 1725-1 Grade 3.2315 T5 Aluminum Tube – Technical Specifications
- DIN 1725-1 Grade 3.4365 T5 – High‑Strength 7075 Aluminum Alloy for Aerospace
- DIN 1725-1 Grade 3.3537 F22 Aluminium Alloy: Superior Strength and Corrosion Resistance
- DIN 1725‑1 Grade 3.4365 O – Premium High‑Strength Aluminum Alloy for Aerospace
- DIN 1725-1 Grade 3.4335 T5 Aluminum Alloy – High-Performance Wrought Grade
- DIN 1725-1 Grade 3.3211 T8 Alloy: Superior Corrosion Resistance & Finish
- DIN 1725-1 Grade 3.0615 T8: High-Performance Free-Cutting Alloy
- DIN 1725-1 Grade 3.1255 T8 Aluminum Alloy – High Strength & Precision Machining
- DIN 1725-1 Grade 3.3537 F: High-Performance AlMg2.7Mn Alloy