EN 10025 Grade S355J2G4C - High-Strength As-Rolled Steel (+AR) for Dynamic Load Applications
S355J2G4C is used for folding, section cold forming and cold drawing grade. The high-tensile fine grained steel is applicable for welding constructions of dynamic load up to -20 °C. Compared to S235J2G4C is achievable a considerable saving of material due to the by 120 MPa higher yield point. The steel shows a by 15% higher resistance to mineral wear due to sliding action in comparison to S235J2G4. Mechanical properties have to comply with EURONORM 164 by arrangement. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll forming grades.
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation | 20.0 °C | 22 % | |
Elongation A80 | 20.0 °C | 14 - 18 % | |
Elongation A80, transverse | 20.0 °C | 12 - 16 % | |
Elongation, transverse | 20.0 °C | 20 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 490 - 680 MPa | |
Yield strength | 20.0 °C | 345 - 355 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Max service temperature, long | -20 - 0 °C | ||
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.2 % |
Manganese | 1.6 % |
Phosphorus | 0.04 % |
Silicon | 0.55 % |
Sulfur | 0.035 % |
Metal
- DIN 5512-1 Grade S355J2G1W Steel – As-Rolled with Annealing (AR)
- DIN 5512-1 Grade S235J2G3C Steel – As-Rolled Condition (AR) – Technical Specs & Applications
- EN 10025 S235J2G4C Steel – As-Rolled Grade for Dynamic Structures
- EN 10025 S235JRC Steel – As‑Rolled (AR) Grade for Construction
- EN 10025 Grade S235JRG1: As-Rolled Steel for Cold-Forming and Welding
- EN 10025 S355K2G4C Steel – High-Tensile, Fine-Grained (As-Rolled + AR)
- EN 10025 Grade S275J0C – As‑Rolled Steel (+AR) for Cold Forming Applications
- EN 10025 S275JRC Steel – As-Rolled (+AR) for Cold Forming & Drawing
- EN 10025 S235JRG2C Steel – As-Rolled (+AR), Ideal for Cold Forming & Welding
- EN 10025 Grade S235J0C – As-Rolled Condition (+AR) – High‑Performance Low‑Carbon Steel