EN 10025 Grade S235J0C – As-Rolled Condition (+AR) – High‑Performance Low‑Carbon Steel
S235JRG2C is used for folding, section cold forming and cold drawing grade. The steel is applicable for welding constructions up to -20 °C subject to the load. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll forming grades.
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation | 20.0 °C | 26 % | |
Elongation A80 | 20.0 °C | 17 - 21 % | |
Elongation A80, transverse | 20.0 °C | 15 - 19 % | |
Elongation, transverse | 20.0 °C | 24 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 340 - 510 MPa | |
Tensile strength, transverse | 20.0 °C | 340 - 510 MPa | |
Yield strength | 20.0 °C | 225 - 235 MPa | |
Yield strength, transverse | 20.0 °C | 225 - 235 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Max service temperature, long | -20 - 0 °C | ||
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.17 % |
Manganese | 1.4 % |
Nitrogen | 9E-3 % |
Phosphorus | 0.04 % |
Sulfur | 0.04 % |
Metal
- DIN 5512-1 Grade S355J2G1W Steel – As-Rolled with Annealing (AR)
- DIN 5512-1 Grade S235J2G3C Steel – As-Rolled Condition (AR) – Technical Specs & Applications
- EN 10025 S235J2G4C Steel – As-Rolled Grade for Dynamic Structures
- EN 10025 S235JRC Steel – As‑Rolled (AR) Grade for Construction
- EN 10025 Grade S235JRG1: As-Rolled Steel for Cold-Forming and Welding
- EN 10025 Grade S355J2G4C - High-Strength As-Rolled Steel (+AR) for Dynamic Load Applications
- EN 10025 S355K2G4C Steel – High-Tensile, Fine-Grained (As-Rolled + AR)
- EN 10025 Grade S275J0C – As‑Rolled Steel (+AR) for Cold Forming Applications
- EN 10025 S275JRC Steel – As-Rolled (+AR) for Cold Forming & Drawing
- EN 10025 S235JRG2C Steel – As-Rolled (+AR), Ideal for Cold Forming & Welding