WL 3.2134 (Grade 3.2134) T6 – High-Performance Castable Welding Alloy
Good weldable cast material with good casting properties. Castings are sensitive to impact loads. Application: fittings
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.7 g/cm³ | T6 | WL 3.2134 | Casting | |
20.0 °C | 2.7 g/cm³ | T6 | WL 3.2134 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 MPa | T6 | WL 3.2134 | Casting | ||
70.0 MPa | T6 | WL 3.2134 | Casting | |||
Elastic modulus | 71.0 GPa | T6 | WL 3.2134 | Casting | ||
20.0 °C | 71.0 GPa | T6 | WL 3.2134 | |||
Elongation | 0.5 % | T6 | WL 3.2134 | Casting | A50 | |
20.0 °C | 0.5 % | T6 | WL 3.2134 | |||
20.0 °C | 1.5 % | T6 | WL 3.2134 | |||
20.0 °C | 2.0 % | T6 | WL 3.2134 | |||
Hardness, Brinell | 75.0 [-] | T6 | WL 3.2134 | Casting | ||
20.0 °C | 75.0 [-] | T6 | WL 3.2134 | |||
20.0 °C | 80.0 [-] | T6 | WL 3.2134 | |||
20.0 °C | 85.0 [-] | T6 | WL 3.2134 | |||
Poisson's ratio | 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | ||||
Shear modulus | 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Shear strength | 20.0 °C | 190.0 MPa | T6 | WL 3.2134 | ||
20.0 °C | 210.0 MPa | T6 | WL 3.2134 | |||
Tensile strength | 190.0 MPa | T6 | WL 3.2134 | Casting | ||
20.0 °C | 190.0 MPa | T6 | WL 3.2134 | |||
20.0 °C | 200.0 MPa | T6 | WL 3.2134 | |||
20.0 °C | 210.0 MPa | T6 | WL 3.2134 | |||
20.0 °C | 220.0 MPa | T6 | WL 3.2134 | |||
20.0 °C | 250.0 MPa | T6 | WL 3.2134 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.2e-05 1/K | T6 | WL 3.2134 | Casting | |
100 °C | 2.2e-05 1/K | T6 | WL 3.2134 | Casting | ||
Melting point | 545.0 - 621.0 °C | T6 | WL 3.2134 | Casting | ||
Specific heat capacity | 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium | ||||
Thermal conductivity | 142.0 - 176.0 W/(m·K) | T6 | WL 3.2134 | Casting |
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 19000000.0 - 25000000.0 S/m | T6 | WL 3.2134 | Casting |
Electrical resistivity | 4e-08 - 5.26e-08 Ω·m | T6 | WL 3.2134 | Casting |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.25 % | T6 | WL 3.2134 | Casting |
Copper | 1.0 - 1.5 % | T6 | WL 3.2134 | Casting |
Iron | 0.6 % | T6 | WL 3.2134 | |
0.60 % | T6 | WL 3.2134 | Casting | |
Magnesium | 0.4 - 0.6 % | T6 | WL 3.2134 | Casting |
Manganese | 0.5 % | T6 | WL 3.2134 | Casting |
Silicon | 4.5 - 5.5 % | T6 | WL 3.2134 | Casting |
Titanium | 0.25 % | T6 | WL 3.2134 | Casting |
Zinc | 0.3 % | T6 | WL 3.2134 | Casting |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | permanent mould casting | |
Metal
- WL 3.2134 H3x: Premium Weldable Cast Material for High-Performance Applications
- WL 3.1754 T6 Alloy – Premium Material for Gearboxes & Air Inlet Systems
- EN 1706 AC-44000 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-44100 F – High-Performance Aluminium Casting Alloy
- EN 1706 Grade AC-44200 F Aluminium Casting Alloy – High-Performance, Industrial Grade
- EN 1706 AC-44300 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-44400F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-51200 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-51300 F – High-Strength Aluminium Casting Alloy
- EN 1706 AC-46500 F – Aluminium Die Casting Alloy: Properties & Standards