WL 3.2134 H3x: Premium Weldable Cast Material for High-Performance Applications
Good weldable cast material with good casting properties. Castings are sensitive to impact loads. Application: fittings
Properties
General
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Density | 20.0 °C | 2.7 g/cm³ | H3x | WL 3.2134 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 71.0 GPa | H3x | WL 3.2134 | |
Elongation | 20.0 °C | 0.5 % | H3x | WL 3.2134 | |
20.0 °C | 1.0 % | H3x | WL 3.2134 | ||
20.0 °C | 1.5 % | H3x | WL 3.2134 | ||
20.0 °C | 2.0 % | H3x | WL 3.2134 | ||
Hardness, Brinell | 20.0 °C | 60.0 [-] | H3x | WL 3.2134 | |
20.0 °C | 65.0 [-] | H3x | WL 3.2134 | ||
20.0 °C | 70.0 [-] | H3x | WL 3.2134 | ||
Poisson's ratio | 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Shear modulus | 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Shear strength | 20.0 °C | 120.0 MPa | H3x | WL 3.2134 | |
20.0 °C | 160.0 MPa | H3x | WL 3.2134 | ||
Tensile strength | 20.0 °C | 150.0 MPa | H3x | WL 3.2134 | |
20.0 °C | 160.0 MPa | H3x | WL 3.2134 | ||
20.0 °C | 180.0 MPa | H3x | WL 3.2134 | ||
20.0 °C | 190.0 MPa | H3x | WL 3.2134 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.3e-05 1/K | Typical for Cast 3xx.x Series Aluminium |
Melting point | 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium |
Specific heat capacity | 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium |
Thermal conductivity | 130.0 - 180.0 W/(m·K) | Typical for Cast 3xx.x Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.25 | H3x | WL 3.2134 |
Copper | 1.0 - 1.5 % | H3x | WL 3.2134 |
Iron | 0.6 | H3x | WL 3.2134 |
Magnesium | 0.4 - 0.6 % | H3x | WL 3.2134 |
Manganese | 0.5 | H3x | WL 3.2134 |
Silicon | 4.5 - 5.5 % | H3x | WL 3.2134 |
Titanium | 0.25 | H3x | WL 3.2134 |
Zinc | 0.3 | H3x | WL 3.2134 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | permanent mould casting | |
Metal
- ASTM A514 Grade F Low-Carbon Steel – Key Properties & Applications
- EN 1652 CuCo1Ni1Be TH – High-Performance Copper Alloy for Industrial Applications
- EN 12163 CuZr TH Grade – High Strength Low‑Alloy Copper Alloy
- EN 12163 Grade CuBe2 M: High-Performance Hardenable Copper Alloy
- EN 10305-5 Grade St 33 Welded Precision Steel Tubes
- BS 3100 Grade A1 Steel Specifications & Properties
- WL 3.2134 H3x: Premium Weldable Cast Material for High-Performance Applications
- WL 3.2364 Cast Alloy – Grade H3x: Superior Weldability & Performance
- WL 3.2364 T5: Superior Weldable Cast Alloy for High-Integrity Applications
- WL 3.2134 (Grade 3.2134) T6 – High-Performance Castable Welding Alloy