EN 573-3 Grade 3.3523 F – High-Performance Marine Aluminum Alloy

Aluminum DIN 3.3523 is a non-heat treatable alloy with excellent finishing qualities. DIN 3.3523 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.

Properties

General

Property	Value	Condition	Related Standards
Density	2.68 g/cm³	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	70.0 GPa	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.3 GPa	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Tensile strength	165.0 MPa	F	EN 573-3, EN 485
	170.0 MPa	F	EN 573-3, EN 755
	180.0 - 250.0 MPa	F	EN 573-3, EN 1715-3

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.2100000000000002e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	20 °C	2.2100000000000002e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	20 °C	2.38e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	20 °C	2.48e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	20 °C	2.5699999999999998e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	100 °C	2.38e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	200 °C	2.48e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	300 °C	2.5699999999999998e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		605.0 - 650.0 °C	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
		607.0 - 649.0 °C	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Specific heat capacity		900.0 J/(kg·K)	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Thermal conductivity		130.0 - 150.0 W/(m·K)	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
		138 W/(m·K)	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	19000000.0 - 21000000.0 S/m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	20000000.0 S/m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Electrical resistivity	4.76e-08 - 5.26e-08 Ω·m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
	5e-08 Ω·m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.15 - 0.35 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Copper	0.1 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Iron	0.40 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Magnesium	2.2 - 2.8 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Manganese	0.1 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Silicon	0.25 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755
Zinc	0.1 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 755

Technological properties

Property
Anodizing	decorative: good, Protective: very good
Corrosion properties	Seawater: very good to good, weathering: good
Workability	Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)

Property

Anodizing

decorative: good, Protective: very good

Corrosion properties

Seawater: very good to good, weathering: good

Workability

Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)