EN 573-3 Aluminum Grade 3.3523 H42 – Superior Corrosion Resistance & Weldability

Aluminum DIN 3.3523 is a non-heat treatable alloy with excellent finishing qualities. DIN 3.3523 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.

Properties

General

Property	Value	Condition	Related Standards
Density	2.68 g/cm³	H42	EN 573-3, EN 1396, EN 541

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending Fatigue Strength	110.0 MPa	H42	EN 573-3, EN 1396, EN 541
Elastic modulus	70.0 GPa	H42	EN 573-3, EN 1396, EN 541
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.3 GPa	H42	EN 573-3, EN 1396, EN 541
Tensile strength	205.0 - 260.0 MPa	H42	EN 573-3, EN 1396
	215.0 - 265.0 MPa	H42	EN 573-3, EN 541

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.2100000000000002e-05 1/K	H42	EN 573-3, EN 1396, EN 541
	20 °C	2.2100000000000002e-05 1/K	H42	EN 573-3, EN 1396, EN 541
	20 °C	2.38e-05 1/K	H42	EN 573-3, EN 1396, EN 541
	20 °C	2.48e-05 1/K	H42	EN 573-3, EN 1396, EN 541
	20 °C	2.5699999999999998e-05 1/K	H42	EN 573-3, EN 1396, EN 541
	100 °C	2.38e-05 1/K	H42	EN 573-3, EN 1396, EN 541
	200 °C	2.48e-05 1/K	H42	EN 573-3, EN 1396, EN 541
	300 °C	2.5699999999999998e-05 1/K	H42	EN 573-3, EN 1396, EN 541
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		605.0 - 650.0 °C	H42	EN 573-3, EN 1396, EN 541
		607.0 - 649.0 °C	H42	EN 573-3, EN 1396, EN 541
Specific heat capacity		900.0 J/(kg·K)	H42	EN 573-3, EN 1396, EN 541
Thermal conductivity		130.0 - 150.0 W/(m·K)	H42	EN 573-3, EN 1396, EN 541
		138 W/(m·K)	H42	EN 573-3, EN 1396, EN 541

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	19000000.0 - 21000000.0 S/m	H42	EN 573-3, EN 1396, EN 541
	20000000.0 S/m	H42	EN 573-3, EN 1396, EN 541
Electrical resistivity	4.76e-08 - 5.26e-08 Ω·m	H42	EN 573-3, EN 1396, EN 541
	5e-08 Ω·m	H42	EN 573-3, EN 1396, EN 541

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.15 - 0.35 %	H42	EN 573-3, EN 1396, EN 541
Copper	0.1 %	H42	EN 573-3, EN 1396, EN 541
Iron	0.40 %	H42	EN 573-3, EN 1396, EN 541
Magnesium	2.2 - 2.8 %	H42	EN 573-3, EN 1396, EN 541
Manganese	0.1 %	H42	EN 573-3, EN 1396, EN 541
Silicon	0.25 %	H42	EN 573-3, EN 1396, EN 541
Zinc	0.1 %	H42	EN 573-3, EN 1396, EN 541

Technological properties

Property
Anodizing	decorative: good, Protective: very good
Corrosion properties	Seawater: very good to good, weathering: good
Workability	Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)

Property

Anodizing

decorative: good, Protective: very good

Corrosion properties

Seawater: very good to good, weathering: good

Workability

Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)