EN 573-3 Grade 3.3523 H111 Aluminum Alloy – Superior Corrosion Resistance & Weldability

Aluminum DIN 3.3523 is a non-heat treatable alloy with excellent finishing qualities. DIN 3.3523 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.

Properties

General

Property	Value	Condition	Related Standards
Density	2.68 g/cm³	H111	EN 573-3, EN 485, EN 754, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending angle 180°	0.5 °/t	H111	EN 573-3, EN 485
Bending angle 90°	0.5 °/t	H111	EN 573-3, EN 485
	1.0 °/t	H111	EN 573-3, EN 485
	2.0 °/t	H111	EN 573-3, EN 485
Elastic modulus	70.0 GPa	H111	EN 573-3, EN 485, EN 754, EN 755
Hardness, Brinell	46.0 [-]	H111	EN 573-3, EN 485
	47.0 [-]	H111	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.3 GPa	H111	EN 573-3, EN 485, EN 754, EN 755
Tensile strength	165.0 - 215.0 MPa	H111	EN 573-3, EN 485
	170.0 - 215.0 MPa	H111	EN 573-3, EN 485
	170.0 - 230.0 MPa	H111	EN 573-3, EN 754, EN 755

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.2100000000000002e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.2100000000000002e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.38e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.48e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.5699999999999998e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	100 °C	2.38e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	200 °C	2.48e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	300 °C	2.5699999999999998e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		605.0 - 650.0 °C	H111	EN 573-3, EN 485, EN 754, EN 755
		607.0 - 649.0 °C	H111	EN 573-3, EN 485, EN 754, EN 755
Specific heat capacity		900.0 J/(kg·K)	H111	EN 573-3, EN 485, EN 754, EN 755
Thermal conductivity		130.0 - 150.0 W/(m·K)	H111	EN 573-3, EN 485, EN 754, EN 755
		138 W/(m·K)	H111	EN 573-3, EN 485, EN 754, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	19000000.0 - 21000000.0 S/m	H111	EN 573-3, EN 485, EN 754, EN 755
	20000000.0 S/m	H111	EN 573-3, EN 485, EN 754, EN 755
Electrical resistivity	4.76e-08 - 5.26e-08 Ω·m	H111	EN 573-3, EN 485, EN 754, EN 755
	5e-08 Ω·m	H111	EN 573-3, EN 485, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.15 - 0.35 %	H111	EN 573-3, EN 485, EN 754, EN 755
Copper	0.1 %	H111	EN 573-3, EN 485, EN 754, EN 755
Iron	0.40 %	H111	EN 573-3, EN 485, EN 754, EN 755
Magnesium	2.2 - 2.8 %	H111	EN 573-3, EN 485, EN 754, EN 755
Manganese	0.1 %	H111	EN 573-3, EN 485, EN 754, EN 755
Silicon	0.25 %	H111	EN 573-3, EN 485, EN 754, EN 755
Zinc	0.1 %	H111	EN 573-3, EN 485, EN 754, EN 755

Technological properties

Property
Anodizing	decorative: good, Protective: very good
Corrosion properties	Seawater: very good to good, weathering: good
Workability	Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)

Property

Anodizing

decorative: good, Protective: very good

Corrosion properties

Seawater: very good to good, weathering: good

Workability

Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)