EN 573-3 Grade 3.3316 O – Premium Al‑Mg Alloy for Superior Corrosion Resistance
The alloys are characterised by a good corrosion resistance. It is sea water steady and resistant to saline atmosphere. The Mg content increases the strength, but the cold forming capacity decreases. The material is nature hard, i.e. only by a cold forming and not by a purposeful heat treatment a strength increase can be attained. It is well polishable and anodisable. The splinter-giving machinability becomes better with increasing Mg content, just as the weldability. From the AlMg alloys the mark AlMg1,5 has to exhibit only relatively small mechanical properties. Standardised semi-finished material only for sheet metal and strips with thickness: > 0.35 mm in accordance to DIN 1745. Application: The main application lies in the building industry. In the building industry for lamella net curtains, rolling shutter, roll gates, in food industry (including table-ware) and for transport containers.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.68 g/cm³ | O | EN 573-3, EN 485 | ||
2.69 g/cm³ | O | EN 573-3, EN 485 | |||
20.0 °C | 2.69 g/cm³ | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending angle 180° | 0.5 °/t | O | EN 573-3, EN 485 | |||
Bending angle 90° | 1.0 °/t | O | EN 573-3, EN 485 | |||
2.0 °/t | O | EN 573-3, EN 485 | ||||
Elastic modulus | 69.0 GPa | O | EN 573-3, EN 485 | |||
70.0 GPa | O | EN 573-3, EN 485 | ||||
20.0 °C | 70.0 GPa | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip | ||
Elongation | 16.0 % | O | EN 573-3, EN 485 | A50 | ||
17.0 % | O | EN 573-3, EN 485 | A50 | |||
19.0 % | O | EN 573-3, EN 485 | A50 | |||
20.0 % | O | EN 573-3, EN 485 | A50 | |||
20.0 % | O | EN 573-3, EN 485 | A100 | |||
21.0 % | O | EN 573-3, EN 485 | A50 | |||
20.0 °C | 20.0 % | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip | A10 | |
20.0 °C | 23.0 % | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip | ||
Hardness, Brinell | 36.0 [-] | O | EN 573-3, EN 485 | |||
20.0 °C | 37.0 [-] | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Shear modulus | 20.0 °C | 26.5 | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip | |
Tensile strength | 20.0 °C | 130.0 - 170.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Sheet, Strip |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K | O | EN 573-3, EN 485 | ||
100 °C | 2.38e-05 1/K | O | EN 573-3, EN 485 | |||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Melting point | 620.0 - 650.0 °C | O | EN 573-3, EN 485 | |||
625.0 - 650.0 °C | O | EN 573-3, EN 485 | ||||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | ||||
Thermal conductivity | 170.0 - 190.0 W/(m·K) | O | EN 573-3, EN 485 | |||
193 W/(m·K) | O | EN 573-3, EN 485 | ||||
20.0 °C | 160.0 - 200.0 W/(m·K) | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 23000000.0 - 26000000.0 S/m | O | EN 573-3, EN 485 | ||
29000000.0 S/m | O | EN 573-3, EN 485 | |||
20.0 °C | 28000000.0 - 30000000.0 S/m | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip | |
Electrical resistivity | 3.45e-08 Ω·m | O | EN 573-3, EN 485 | ||
3.85e-08 - 4.35e-08 Ω·m | O | EN 573-3, EN 485 |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % | O | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Sheet, Strip |
Copper | 0.05 % | O | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Sheet, Strip |
Iron | 0.45 % | O | DIN 1725-1, EN 573-3, EN 573-4 | Sheet, Strip |
0.45 % | O | EN 573-3, EN 485 | ||
Magnesium | 1.1 - 1.7 % | O | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Sheet, Strip |
Manganese | 0.15 % | O | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Sheet, Strip |
Silicon | 0.4 % | O | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Sheet, Strip |
Zinc | 0.2 % | O | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Sheet, Strip |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- EN 573-3 Grade 3.3316 F – Key Properties & Standards for 5000 Series Aluminium
- EN 573-3 Grade 3.3316 H44 Aluminium – Detailed Properties
- EN 573-3 Grade 3.3316 H46 – Aluminum Alloy Properties
- EN 573-3 Grade 3.3316 H48 Aluminum Alloy – Key Properties & Standards
- EN 573-3 Grade 3.3316 H49 – Key Material Specs & Standards
- EN 573-3 Grade 3.3316 H112: Detailed Material Properties & Standards
- EN 573-3 Grade 3.3316 H12 – Premium Aluminium for High-Performance Applications
- EN 573-3 Grade 3.3316 H14 Steel – Comprehensive Properties & Standards
- EN 573-3 Grade 3.3316 H26 Steel – Specifications & Mechanical Properties
- EN 573-3 Grade 3.3316 H36 – Steel Specifications & Standards