EN 573-3 Grade 3.3523 H26 Aluminum Alloy – Superior Corrosion Resistance & Welding Performance

Aluminum DIN 3.3523 is a non-heat treatable alloy with excellent finishing qualities. DIN 3.3523 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.

Properties

General

Property	Value	Condition	Related Standards
Density	2.68 g/cm³	H26	EN 573-3, EN 485, EN 541, EN 754

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending Fatigue Strength	125.0 MPa	H26	EN 573-3, EN 485, EN 541, EN 754
Bending angle 90°	1.5 °/t	H26	EN 573-3, EN 485
	2.0 °/t	H26	EN 573-3, EN 485
	3.0 °/t	H26	EN 573-3, EN 485
	3.5 °/t	H26	EN 573-3, EN 485
Elastic modulus	70.0 GPa	H26	EN 573-3, EN 485, EN 541, EN 754
Hardness, Brinell	74.0 [-]	H26	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.3 GPa	H26	EN 573-3, EN 485, EN 541, EN 754
Tensile strength	250.0 - 300.0 MPa	H26	EN 573-3, EN 485
	250.0 - 290.0 MPa	H26	EN 573-3, EN 754
	260.0 - 300.0 MPa	H26	EN 573-3, EN 541

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.2100000000000002e-05 1/K	H26	EN 573-3, EN 485, EN 541, EN 754
	20 °C	2.2100000000000002e-05 1/K	H26	EN 573-3, EN 485, EN 541, EN 754
	20 °C	2.38e-05 1/K	H26	EN 573-3, EN 485, EN 541, EN 754
	20 °C	2.48e-05 1/K	H26	EN 573-3, EN 485, EN 541, EN 754
	20 °C	2.5699999999999998e-05 1/K	H26	EN 573-3, EN 485, EN 541, EN 754
	100 °C	2.38e-05 1/K	H26	EN 573-3, EN 485, EN 541, EN 754
	200 °C	2.48e-05 1/K	H26	EN 573-3, EN 485, EN 541, EN 754
	300 °C	2.5699999999999998e-05 1/K	H26	EN 573-3, EN 485, EN 541, EN 754
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		605.0 - 650.0 °C	H26	EN 573-3, EN 485, EN 541, EN 754
		607.0 - 649.0 °C	H26	EN 573-3, EN 485, EN 541, EN 754
Specific heat capacity		900.0 J/(kg·K)	H26	EN 573-3, EN 485, EN 541, EN 754
Thermal conductivity		130.0 - 150.0 W/(m·K)	H26	EN 573-3, EN 485, EN 541, EN 754
		138 W/(m·K)	H26	EN 573-3, EN 485, EN 541, EN 754

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	19000000.0 - 21000000.0 S/m	H26	EN 573-3, EN 485, EN 541, EN 754
	20000000.0 S/m	H26	EN 573-3, EN 485, EN 541, EN 754
Electrical resistivity	4.76e-08 - 5.26e-08 Ω·m	H26	EN 573-3, EN 485, EN 541, EN 754
	5e-08 Ω·m	H26	EN 573-3, EN 485, EN 541, EN 754

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.15 - 0.35 %	H26	EN 573-3, EN 485, EN 541, EN 754
Copper	0.1 %	H26	EN 573-3, EN 485, EN 541, EN 754
Iron	0.40 %	H26	EN 573-3, EN 485, EN 541, EN 754
Magnesium	2.2 - 2.8 %	H26	EN 573-3, EN 485, EN 541, EN 754
Manganese	0.1 %	H26	EN 573-3, EN 485, EN 541, EN 754
Silicon	0.25 %	H26	EN 573-3, EN 485, EN 541, EN 754
Zinc	0.1 %	H26	EN 573-3, EN 485, EN 541, EN 754

Technological properties

Property
Anodizing	decorative: good, Protective: very good
Corrosion properties	Seawater: very good to good, weathering: good
Workability	Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)

Property

Anodizing

decorative: good, Protective: very good

Corrosion properties

Seawater: very good to good, weathering: good

Workability

Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)