Aluminum DIN 3.3523 H19 – Superior Corrosion Resistance & Welding Performance
Aluminum DIN 3.3523 is a non-heat treatable alloy with excellent finishing qualities. DIN 3.3523 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.68 g/cm³ | H19 | EN 573-3, EN 541 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa | H19 | EN 573-3, EN 541 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.3 GPa | H19 | EN 573-3, EN 541 | |
Tensile strength | 300.0 - 360.0 MPa | H19 | EN 573-3, EN 541 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.2100000000000002e-05 1/K | H19 | EN 573-3, EN 541 | |
20 °C | 2.2100000000000002e-05 1/K | H19 | EN 573-3, EN 541 | ||
20 °C | 2.38e-05 1/K | H19 | EN 573-3, EN 541 | ||
20 °C | 2.48e-05 1/K | H19 | EN 573-3, EN 541 | ||
20 °C | 2.5699999999999998e-05 1/K | H19 | EN 573-3, EN 541 | ||
100 °C | 2.38e-05 1/K | H19 | EN 573-3, EN 541 | ||
200 °C | 2.48e-05 1/K | H19 | EN 573-3, EN 541 | ||
300 °C | 2.5699999999999998e-05 1/K | H19 | EN 573-3, EN 541 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 605.0 - 650.0 °C | H19 | EN 573-3, EN 541 | ||
607.0 - 649.0 °C | H19 | EN 573-3, EN 541 | |||
Specific heat capacity | 900.0 J/(kg·K) | H19 | EN 573-3, EN 541 | ||
Thermal conductivity | 130.0 - 150.0 W/(m·K) | H19 | EN 573-3, EN 541 | ||
138 W/(m·K) | H19 | EN 573-3, EN 541 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 19000000.0 - 21000000.0 S/m | H19 | EN 573-3, EN 541 |
20000000.0 S/m | H19 | EN 573-3, EN 541 | |
Electrical resistivity | 4.76e-08 - 5.26e-08 Ω·m | H19 | EN 573-3, EN 541 |
5e-08 Ω·m | H19 | EN 573-3, EN 541 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.15 - 0.35 % | H19 | EN 573-3, EN 541 |
Copper | 0.1 % | H19 | EN 573-3, EN 541 |
Iron | 0.40 % | H19 | EN 573-3, EN 541 |
Magnesium | 2.2 - 2.8 % | H19 | EN 573-3, EN 541 |
Manganese | 0.1 % | H19 | EN 573-3, EN 541 |
Silicon | 0.25 % | H19 | EN 573-3, EN 541 |
Zinc | 0.1 % | H19 | EN 573-3, EN 541 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: good, Protective: very good | |
| Corrosion properties | Seawater: very good to good, weathering: good | |
| Workability | Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12) | |
Metal
- EN 573-3 Grade 3.0505 H19 – Premium Wrought Aluminum Alloy
- EN 573-3 Grade 3.0515 H19 Aluminium: Properties, Standards, and Applications
- EN 573-3 Grade 3.3315 H19 Aluminium – Specifications & Properties
- EN 573-3 Grade 3.3549 H19 – High-Performance Alloy with Superior Strength
- EN 573-3 Grade 3.0257 H19 Aluminium – Specifications & Performance
- EN 573-3 Grade 3.3206 H19 – High-Performance Aluminium Alloy
- EN 573-3 Grade 3.0525 H19 – Premium Aluminium Alloy Specification
- EN 573-3 Grade 3.0526 H19 Aluminium – Properties & Standards
- EN 573-3 Grade 3.0205 H19 – Certified Aluminium Alloy Properties
- EN 573-3 Grade 3.3523 F – High-Performance Marine Aluminum Alloy