Pure Nickel – 205 GPa Elastic Modulus, 449 MPa Tensile Strength, Multi‑width Availability
Commercially pure, unalloyed Nickel.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.89 g/cm³ |
Dimension
| Property | Value |
|---|---|
Width | 3.18 - 57.15 mm |
Dimensions | Available widths: 3.2mm, 4.8mm, 6.4mm, 7.9mm, 9.5mm, 12.7mm, 15.9mm, 19.1mm, 22.2mm, 28.6mm, 31.8mm, 44.5mm, 50.8mm, 57.2mm |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 207 GPa | |
Elongation | 23.0 °C | 40 % | in 2 in. |
Hardness, Rockwell B | 23.0 °C | 80 [-] | |
Tensile strength | 23.0 °C | 449 MPa | |
Yield strength | 23.0 °C | 138 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.3E-5 1/K | from 30°C to the mentioned temperature |
Melting point | 1440 °C | ||
Specific heat capacity | 23.0 °C | 452 J/(kg·K) | |
Thermal conductivity | 23.0 °C | 75 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 9.5E-8 Ω·m |
Magnetic
| Property | Value |
|---|---|
Curie temperature | 360 °C |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.07 % |
Iron | 0.2 % |
Magnesium | 0.01 - 0.1 % |
Nickel | 99.5 % |
Silicon | 0.15 % |
Sulfur | 8E-3 % |
Titanium | 0.05 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Common applications of Nickel 205: Getter tabs, heating element sheathing, anodes, fuel cells, special purpose electron tubes, transistor enclosures, cathode shields, spark gaps | |
Metal
- EN AW 6082 Round Bar – Premium Aluminum Alloy for Engineering & Decorative Applications
- EN AW 2007 Round Bar – High-Quality AlCu4PbMgMn for Precision Machining
- Nickel 270 – Commercially Pure, Unalloyed Nickel for Industrial Use
- BS NS101 Nickel Silver: Premium Corrosion‑Resistant Alloy for Electronics & Architecture
- BS NS104 Nickel Silver – Premium Sheet Metal with Superior Strength & Corrosion Resistance
- Commercial Nickel 201 Bar – High Purity, Unalloyed Nickel for Industrial Applications
- Commercial Nickel 205 Sheet – 207 GPa Modulus, 449 MPa Strength
- Commercially Pure Nickel Bar 233 – High-Strength, Unalloyed Nickel for Industrial Applications
- Alloy 52 Bar: High-Performance Nickel-Iron Steel with Superior Strength
- Commercial Nickel 200 Bar – Pure, Unalloyed, High‑Strength Material