EN 573-3 Grade 3.1355 T42 Aluminum Alloy – High Strength & Machinability for Aerospace

Aluminum DIN 3.1355, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.

Properties

General

Property	Value	Condition	Related Standards
Density	2.77 g/cm³	T42	EN 573-3, EN 485, EN 603
	2.78 g/cm³	T42	EN 573-3, EN 485, EN 603

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	73.0 GPa	T42	EN 573-3, EN 485, EN 603
Hardness, Brinell	118.0 [-]	T42	EN 573-3, EN 485
	119.0 [-]	T42	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 2000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 2000 Series Aluminium
Shear modulus	27.4 GPa	T42	EN 573-3, EN 485, EN 603
Tensile strength	420.0 MPa	T42	EN 573-3, EN 603
	425.0 MPa	T42	EN 573-3, EN 485

Thermal

Property	Temperature	Value	Condition	Related Standards
Coefficient of thermal expansion	-50 °C	2.11e-05 1/K	T42	EN 573-3, EN 485, EN 603
	20 °C	2.11e-05 1/K	T42	EN 573-3, EN 485, EN 603
	20 °C	2.2899999999999998e-05 1/K	T42	EN 573-3, EN 485, EN 603
	20 °C	2.3199999999999998e-05 1/K	T42	EN 573-3, EN 485, EN 603
	20 °C	2.38e-05 1/K	T42	EN 573-3, EN 485, EN 603
	20 °C	2.4699999999999997e-05 1/K	T42	EN 573-3, EN 485, EN 603
	100 °C	2.2899999999999998e-05 1/K	T42	EN 573-3, EN 485, EN 603
	100 °C	2.3199999999999998e-05 1/K	T42	EN 573-3, EN 485, EN 603
	200 °C	2.38e-05 1/K	T42	EN 573-3, EN 485, EN 603
	300 °C	2.4699999999999997e-05 1/K	T42	EN 573-3, EN 485, EN 603
Melting point		505.0 - 640.0 °C	T42	EN 573-3, EN 485, EN 603
		505.0 - 635.0 °C	T42	EN 573-3, EN 485, EN 603
Specific heat capacity		875.0 J/(kg·K)	T42	EN 573-3, EN 485, EN 603
Thermal conductivity		121.0 - 193.0 W/(m·K)	T42	EN 573-3, EN 485, EN 603
		130.0 - 150.0 W/(m·K)	T42	EN 573-3, EN 485, EN 603

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	17000000.0 - 29000000.0 S/m	T42	EN 573-3, EN 485, EN 603
	18000000.0 - 21000000.0 S/m	T42	EN 573-3, EN 485, EN 603
Electrical resistivity	3.45e-08 - 5.88e-08 Ω·m	T42	EN 573-3, EN 485, EN 603
	4.76e-08 - 5.56e-08 Ω·m	T42	EN 573-3, EN 485, EN 603

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.1 %	T42	EN 573-3, EN 485, EN 603
Copper	3.8 - 4.9 %	T42	EN 573-3, EN 485, EN 603
Iron	0.50 %	T42	EN 573-3, EN 485, EN 603
Magnesium	1.2 - 1.8 %	T42	EN 573-3, EN 485, EN 603
Manganese	0.3 - 0.9 %	T42	EN 573-3, EN 485, EN 603
Silicon	0.5 %	T42	EN 573-3, EN 485, EN 603
Titanium	0.15 %	T42	EN 573-3, EN 485, EN 603
Zinc	0.25 %	T42	EN 573-3, EN 485, EN 603

Technological properties

Property
Anodizing	decorative: not suitable, Protective: good
Brazing	hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable
Corrosion properties	Seawater: poor, weathering: poor
Workability	Bending / Spinning (cold): sufficient (O) / acceptable (O), Impact extrusion (cold): acceptable (O), Deep drawing / upsetting (Condition) acceptable (O) / sufficient (O)

EN 573-3 Grade 3.1255 T62 – Premium Heat‑Treatable Aluminum Alloy EN 573-3 Aluminum 3.1355 T62 – High‑Strength Alloy for Aerospace Applications