EN 573-3 Grade AW-6061 H111 – Premium Aluminum Alloy for Corrosion Resistance & Easy Fabrication

EN AW-6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.

Quantity: 1 PCS

BIKAR-METALLE GMBH

MANUFACTURER AND DISTRIBUTOR

Information and services

Additional services: Cuttings, Parts from drawings

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.7 g/cm³	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	20.0 °C	2.7 g/cm³	H111	EN 573-3	Rod, Tube

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus		69.0 GPa	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
		70.0 GPa	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	20.0 °C	68.3 - 69.6 GPa	H111	EN 573-3	Rod, Tube
Elongation		14.0 %	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar	A50
		16.0 %	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar	A100
	20.0 °C	14.0 %	H111	EN 573-3	Rod, Tube	A50
	20.0 °C	16.0 %	H111	EN 573-3	Rod, Tube
Hardness, Brinell	20.0 °C	30.0 [-]	H111	EN 573-3	Rod, Tube
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 6000 Series Aluminium
Shear modulus		26.3 GPa	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	20.0 °C	26.2 GPa	H111	EN 573-3	Rod, Tube
Tensile strength		150.0	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	20.0 °C	150.0	H111	EN 573-3	Rod, Tube

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape
Coefficient of thermal expansion	20 °C	2.3e-05 1/K	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	20 °C	2.36e-05 1/K	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	100 °C	2.3e-05 1/K	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	100 °C	2.36e-05 1/K	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
Melting point		580.0 - 640.0 °C	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
		580.0 - 650.0 °C	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
Specific heat capacity	20.0 °C	870.0 J/(kg·K)	H111	EN 573-3	Rod, Tube
Thermal conductivity		155.0 - 180.0 W/(m·K)	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
		170.0 - 200.0 W/(m·K)	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	20.0 °C	150.0 - 165.0 W/(m·K)	H111	EN 573-3	Rod, Tube

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity		22000000.0 - 30000000.0 S/m	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
		23000000.0 - 27000000.0 S/m	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
	20.0 °C	20000000.0 - 30000000.0 S/m	H111	EN 573-3	Rod, Tube
Electrical resistivity		3.33e-08 - 4.55e-08 Ω·m	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
		3.7e-08 - 4.35e-08 Ω·m	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.04 - 0.35 %	H111	EN 573-3, EN 754, EN 755	Rod, Tube, Strip, Sheet, Plate, Wire, Bar
Copper	0.15 - 0.4 %	H111	EN 573-3, EN 754, EN 755	Rod, Tube, Strip, Sheet, Plate, Wire, Bar
Iron	0.7 %	H111	EN 573-3	Rod, Tube
	0.70 %	H111	EN 573-3, EN 754, EN 755	Strip, Sheet, Plate, Wire, Tube, Bar
Magnesium	0.8 - 1.2 %	H111	EN 573-3, EN 754, EN 755	Rod, Tube, Strip, Sheet, Plate, Wire, Bar
Manganese	0.15 %	H111	EN 573-3, EN 754, EN 755	Rod, Tube, Strip, Sheet, Plate, Wire, Bar
Silicon	0.4 - 0.8 %	H111	EN 573-3, EN 754, EN 755	Rod, Tube, Strip, Sheet, Plate, Wire, Bar
Titanium	0.15 %	H111	EN 573-3, EN 754, EN 755	Rod, Tube, Strip, Sheet, Plate, Wire, Bar
Zinc	0.25 %	H111	EN 573-3, EN 754, EN 755	Rod, Tube, Strip, Sheet, Plate, Wire, Bar

Technological properties

Property
Anodizing	decorative: acceptable, Protective: very good
Brazing	hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable
Corrosion properties	Seawater: good to acceptable, weathering: good
Workability	Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O)