EN 573-3 Grade AW-6061 T39 – Premium Aluminum Alloy for Anodizing & Corrosion Resistance
EN AW-6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.
Quantity: 1 PCSBIKAR-METALLE GMBH
MANUFACTURER AND DISTRIBUTOR
Information and services
Additional services: Cuttings, Parts from drawingsProperties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.7 g/cm³ | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
20.0 °C | 2.7 g/cm³ | T39 | EN 573-3 | Wire |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 69.0 GPa | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | ||
70.0 GPa | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |||
20.0 °C | 68.3 - 69.6 GPa | T39 | EN 573-3 | Wire | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Shear modulus | 26.3 GPa | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | ||
20.0 °C | 26.2 GPa | T39 | EN 573-3 | Wire | ||
Tensile strength | 260.0 MPa | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | ||
310.0 MPa | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |||
20.0 °C | 260.0 MPa | T39 | EN 573-3 | Wire | ||
20.0 °C | 310.0 MPa | T39 | EN 573-3 | Wire |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar |
20 °C | 2.36e-05 1/K | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
100 °C | 2.3e-05 1/K | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
100 °C | 2.36e-05 1/K | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
Melting point | 580.0 - 640.0 °C | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
580.0 - 650.0 °C | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | ||
Specific heat capacity | 20.0 °C | 870.0 J/(kg·K) | T39 | EN 573-3 | Wire |
Thermal conductivity | 155.0 - 180.0 W/(m·K) | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
170.0 - 200.0 W/(m·K) | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | ||
20.0 °C | 150.0 - 165.0 W/(m·K) | T39 | EN 573-3 | Wire |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 22000000.0 - 30000000.0 S/m | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
23000000.0 - 27000000.0 S/m | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | ||
20.0 °C | 20000000.0 - 30000000.0 S/m | T39 | EN 573-3 | Wire | |
Electrical resistivity | 3.33e-08 - 4.55e-08 Ω·m | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
3.7e-08 - 4.35e-08 Ω·m | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.04 - 0.35 % | T39 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Copper | 0.15 - 0.4 % | T39 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Iron | 0.7 % | T39 | EN 573-3 | Wire |
0.70 % | T39 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Wire, Tube, Bar | |
Magnesium | 0.8 - 1.2 % | T39 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Manganese | 0.15 % | T39 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Silicon | 0.4 - 0.8 % | T39 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Titanium | 0.15 % | T39 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Zinc | 0.25 % | T39 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
| Corrosion properties | Seawater: good to acceptable, weathering: good | |
| Workability | Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O) | |
Metal
- EN 573-3 Grade 3.3206 T39 – Premium Aluminium Alloy for High-Performance Applications
- EN 573-3 Grade 3.2315 T39 Aluminium Alloy – Key Mechanical Properties
- AW-6056 T39: Age-Hardenable 6000-Series Aluminium Alloy – EN 573-3 Grade
- EN 573-3 Grade 3.3211 T39 – Premium Anodizable Aluminum Alloy
- EN 573-3 AW-6063 T39 Aluminum Alloy – High Corrosion Resistance & Superior Finish
- AW-6082 T39 Aluminium Alloy – Grade EN 573‑3 for Food‑Safe Applications
- EN 573-3 Grade AW-6061 H18 Aluminum Alloy – Superior Corrosion Resistance & Weldability
- EN 573-3 Grade AW-6061 O3 – Premium Aluminum Alloy for Corrosion Resistance
- EN 573-3 AW-6061 F Aluminum Alloy – Premium, Corrosion-Resistant, Weldable 6061 Grade
- EN 573-3 Grade AW-6061 H111 – Premium Aluminum Alloy for Corrosion Resistance & Easy Fabrication