EN 573-3 Grade 3.0515 O: Premium Al-Mn Alloy with Enhanced Strength and Corrosion Resistance
The alloy AlMn1 is an Al-Mn alloy, which belongs to the nature-hard aluminum materials. Mn increases the strength compared with pure aluminium, but it does not impair the corrosion resistance. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occur by cold forming. It is very well formable, very well corrosion resistant and weldable. In these characteristics it resembles the pure aluminium, but with the attainable strength it exceeds this. The alloy AlMn1 has a increased heat resistance compared with pure aluminium, as result of the of the Mn-additive (inhibits recrystallisation). Application: In the building industry for roofings, as outer skin of buildings, in the apparatus and tank construction as heat exchanger (bank of tubes, profiles, gilled pipes, sheet metals), for radiators, air conditioning systems, pipings for compressed gas tanks, for tanks according VdTUEV Werkstoffblaetter, as antennas for radio relay link and satellite communication (mirror) for technical flow pressed parts, for solid rivets, for generally metal-describe, in food industry (including commercial devices), in the construction of vehicles (including tank cars) and as packing (sheet metal packings generally).
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.73 g/cm³ | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | ||
20.0 °C | 2.73 g/cm³ | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Sheet, Strip, Tube, Wire |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 50.0 MPa | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | |||
Bending angle 180° | 1.0 °/t | O | EN 573-3, EN 485 | |||
Bending angle 90° | 1.0 °/t | O | EN 573-3, EN 485 | |||
1.5 °/t | O | EN 573-3, EN 485 | ||||
Elastic modulus | 69.5 GPa | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | |||
20.0 °C | 60.0 - 65.0 GPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Sheet, Strip, Tube, Wire | ||
Elongation | -196.0 °C | 46.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | ||
-80.0 °C | 42.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
-20.0 °C | 41.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
7.0 % | O | EN 573-3, EN 546 | A50 | |||
8.0 % | O | EN 573-3, EN 546 | A50 | |||
12.0 % | O | EN 573-3, EN 546, EN 683 | A50 | |||
15.0 % | O | EN 573-3, EN 546, EN 683 | A50 | |||
17.0 % | O | EN 573-3, EN 485 | A50 | |||
18.0 % | O | EN 573-3, EN 683 | A50 | |||
19.0 % | O | EN 573-3, EN 485 | A50 | |||
20.0 % | O | EN 573-3, EN 754, EN 755 | A50 | |||
21.0 % | O | EN 573-3, EN 485 | A50 | |||
24.0 % | O | EN 573-3, EN 485 | A50 | |||
25.0 % | O | EN 573-3, EN 485, EN 754, EN 755 | A100 | |||
28.0 % | O | EN 573-3, EN 485 | A50 | |||
35.0 % | O | EN 573-3, EN 1301 | ||||
20.0 °C | 16.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Wire | A100 | |
20.0 °C | 19.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod | A10 | |
20.0 °C | 20.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Tube, Wire | A10 | |
20.0 °C | 21.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Sheet, Strip | A10 | |
20.0 °C | 22.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Tube | ||
20.0 °C | 24.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Sheet, Strip | ||
20.0 °C | 40.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
100.0 °C | 43.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
150.0 °C | 47.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
200.0 °C | 60.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
260.0 °C | 65.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
320.0 °C | 70.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
370.0 °C | 70.0 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
Hardness, Brinell | 27.0 [-] | O | EN 573-3, EN 485 | |||
20.0 °C | 25.0 [-] | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Wire | ||
20.0 °C | 28.0 [-] | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Sheet, Strip | ||
20.0 °C | 30.0 [-] | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Tube | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||||
Shear modulus | 26.1 GPa | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | |||
20.0 °C | 24.0 - 26.5 GPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Sheet, Strip, Tube, Wire | ||
Tensile strength | -196.0 °C | 232.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | ||
-80.0 °C | 137.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
-20.0 °C | 119.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
80.0 - 130.0 MPa | O | EN 573-3, EN 546, EN 683 | ||||
90.0 - 130.0 MPa | O | EN 573-3, EN 485 | ||||
95.0 - 130.0 MPa | O | EN 573-3, EN 754 | ||||
95.0 - 135.0 MPa | O | EN 573-3, EN 755 | ||||
130.0 MPa | O | EN 573-3, EN 1301 | ||||
20.0 °C | 90.0 - 140.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Sheet, Strip | ||
20.0 °C | 95.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Tube, Wire | ||
20.0 °C | 112.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
100.0 °C | 91.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
150.0 °C | 77.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
200.0 °C | 57.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
260.0 °C | 47.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
320.0 °C | 28.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
370.0 °C | 19.0 MPa | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.35e-05 1/K | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | |
100 °C | 2.35e-05 1/K | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | ||
Melting point | 645.0 - 655.0 °C | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | ||
Specific heat capacity | 893.0 J/(kg·K) | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | ||
20.0 °C | 893.0 J/(kg·K) | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Sheet, Strip, Tube, Wire | |
Thermal conductivity | 20.0 °C | 160.0 - 200.0 W/(m·K) | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | Rod, Sheet, Strip, Tube, Wire |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 22000000.0 - 28000000.0 S/m | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | Rod, Sheet, Strip, Tube, Wire |
Electrical resistivity | 3.57e-08 - 4.55e-08 Ω·m | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | Rod, Sheet, Strip, Tube, Wire |
Copper | 0.1 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | Rod, Sheet, Strip, Tube, Wire |
Iron | 0.7 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Sheet, Strip, Tube, Wire |
0.70 % | O | EN 573-3, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | ||
Magnesium | 0.3 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | Rod, Sheet, Strip, Tube, Wire |
Manganese | 0.9 - 1.5 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | Rod, Sheet, Strip, Tube, Wire |
Silicon | 0.5 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | Rod, Sheet, Strip, Tube, Wire |
Titanium | 0.1 | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Rod, Sheet, Strip, Tube, Wire |
Zinc | 0.2 % | O | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 485, EN 546, EN 683, EN 754, EN 755 | Rod, Sheet, Strip, Tube, Wire |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- EN 573-3 Grade 3.0515 O3 – Key Mechanical & Thermal Properties
- AW-8014 O – Food-Safe, High-Performance Aluminum Alloy (EN 573-3)
- AW-8111 O Aluminium Alloy – EN 573‑3 Grade, Food Safe & High Strength
- EN 573-3 Grade AW-2091: Premium Age-Hardenable AlCu Alloy for Structural Applications
- EN 573-3 Grade 3.0515 H19 Aluminium: Properties, Standards, and Applications
- EN 573-3 Grade 3.0515 H38 – High‑Performance Aluminium with Superior Mechanical Properties
- EN 573-3 Grade 3.0515 H44 – High‑Strength Aluminum Alloy Specs
- EN 573-3 Grade 3.0515 H48 – Key Mechanical Properties & Standards
- DIN 1725-1 Grade 3.0515 F – High‑Strength Al‑Mn Alloy for Superior Performance
- EN 573-3 Grade 3.0526 H28 – High Strength, Corrosion‑Resistant Aluminum Alloy