DIN 1725-1 Grade 3.0515 H18 Tubes – Ribbed Specifications for Steam Boiler Applications
Valid for tube with ribbs - outer diameter of ribbed parts of tubes: 36,0 to 70,0 mm - wall thicknes of ribbed parts of tubes: 1,0 to 8,5 mm - spacing of ribbs: 2,2 to 5,1 mm - high of ribbs: 6,5 to 16 mm - average thickness of ribbs: 0,4 to 1,0 mm Melting: - inductive - gaseous heated melting oven Application: - steam boiler with pressure ab to 10 bar Further processing: - no heat treatment
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.73 g/cm³ | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
20.0 °C | 2.73 g/cm³ | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 75.0 MPa | H18 | EN 573-3, EN 1301, EN 485, EN 683, EN 754 | |||
Bending angle 90° | 1.5 °/t | H18 | EN 573-3, EN 485 | |||
2.5 °/t | H18 | EN 573-3, EN 485 | ||||
3.0 °/t | H18 | EN 573-3, EN 485 | ||||
Elastic modulus | 69.5 GPa | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | |||
20.0 °C | 60.0 - 65.0 GPa | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire | ||
Elongation | -196.0 °C | 30.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | ||
-80.0 °C | 18.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
-20.0 °C | 16.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
1.0 % | H18 | EN 573-3, EN 485, EN 546, EN 683 | A50 | |||
2.0 % | H18 | EN 573-3, EN 1592 | A100 | |||
2.0 % | H18 | EN 573-3, EN 485, EN 754 | A50 | |||
3.0 % | H18 | EN 573-3, EN 1301 | ||||
3.0 % | H18 | EN 573-3, EN 754 | A100 | |||
20.0 °C | 1.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Wire | A100 | |
20.0 °C | 3.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire | A10 | |
20.0 °C | 4.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat | ||
20.0 °C | 10.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
100.0 °C | 10.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
150.0 °C | 11.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
200.0 °C | 18.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
260.0 °C | 60.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
320.0 °C | 70.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
370.0 °C | 70.0 % | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | |||
Hardness, Brinell | 58.0 [-] | H18 | EN 573-3, EN 485 | |||
20.0 °C | 45.0 [-] | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Wire | ||
20.0 °C | 50.0 [-] | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||||
Shear modulus | 26.1 GPa | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | |||
20.0 °C | 24.0 - 26.5 GPa | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire | ||
Tensile strength | -196.0 °C | 298.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | ||
-80.0 °C | 225.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
-20.0 °C | 214.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
170.0 MPa | H18 | EN 573-3, EN 1301 | ||||
180.0 MPa | H18 | EN 573-3, EN 754 | ||||
185.0 MPa | H18 | EN 573-3, EN 485, EN 683 | ||||
185.0 - 230.0 MPa | H18 | EN 573-3, EN 546 | ||||
190.0 MPa | H18 | EN 573-3, EN 1592 | ||||
20.0 °C | 100.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513 | Tube | ||
20.0 °C | 160.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | Wire | ||
20.0 °C | 165.0 - 205.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | Flat | ||
20.0 °C | 204.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
100.0 °C | 183.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
150.0 °C | 163.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
200.0 °C | 98.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
260.0 °C | 53.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
320.0 °C | 28.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | |||
370.0 °C | 21.0 MPa | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.35e-05 1/K | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | |
100 °C | 2.35e-05 1/K | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
Melting point | 645.0 - 655.0 °C | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
Specific heat capacity | 893.0 J/(kg·K) | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
20.0 °C | 893.0 J/(kg·K) | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4 | Flat, Wire | |
Thermal conductivity | 20.0 °C | 160.0 - 200.0 W/(m·K) | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Flat, Wire |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 22000000.0 - 28000000.0 S/m | H18 | DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Flat, Wire |
Electrical resistivity | 3.57e-08 - 4.55e-08 Ω·m | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Copper | 0.1 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Iron | 0.7 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | Tube, Flat, Wire |
0.70 % | H18 | EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | ||
Magnesium | 0.3 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Manganese | 0.9 - 1.5 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Silicon | 0.5 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Titanium | 0.1 | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4 | Tube, Flat, Wire |
Zinc | 0.2 % | H18 | DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754 | Tube, Flat, Wire |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- DIN 1725-1 Grade 3.0515 H22 – Comprehensive Aluminium Properties
- DIN 1725-1 Grade 3.0515 H24 Aluminium: Key Properties & Performance
- DIN 1725-1 Grade 3.0915 H18 – High‑Strength AlFeSi Alloy for Precision Forming
- DIN 1725-1 Grade 3.3206 H18: High-Performance Ribbed Aluminium Tubes for Steam Boilers
- DIN 1725-1 Alloy 3.3326 H18 – Superior Seawater Corrosion Resistance & Strength
- DIN 1725-1 Grade 3.0505 H18 – High‑Strength Aluminum Alloy for Advanced Applications
- DIN 1725-1 Grade 3.0515 F – High‑Strength Al‑Mn Alloy for Superior Performance
- DIN 1725-1 Grade 3.3547 H18 – Premium Cold-Worked AlMg4.5Mn Alloy with Superior Corrosion Resistance
- DIN 1725-1 Grade 3.3316 H18 – High-Strength, Corrosion-Resistant Aluminum-Magnesium Alloy
- DIN 1725-1 Grade 3.3315 H18 Aluminum Magnesium Alloy – Corrosion Resistant & Strong