DIN 17210 22CrMoS3-5 Steel: Cold Shearing (+S) Treatment Overview
The steel 22 CrMoS 3 5 is used for wear loaded parts in the vehicle and mechanical engineering with medium core strength, better machinability, high toughness and high fatigue strength (e.g. gears, shafts, axles). The lowest application amounts to -60 °C, the best application up to 60 mm nominal size.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.83 - 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa | |
20.0 °C | 210 - 212 GPa | ||
100.0 °C | 205 - 207 GPa | ||
200.0 °C | 195 - 199 GPa | ||
300.0 °C | 185 - 192 GPa | ||
400.0 °C | 184 GPa | ||
500.0 °C | 175 GPa | ||
600.0 °C | 164 GPa | ||
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Chromium Molybdenum Steel |
Shear modulus | 20.0 °C | 81 GPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.05E-5 1/K | |
20.0 °C | 1.15E-5 1/K | ||
100.0 °C | 1.11E-5 - 1.21E-5 1/K | ||
200.0 °C | 1.21E-5 - 1.27E-5 1/K | ||
300.0 °C | 1.29E-5 - 1.32E-5 1/K | ||
400.0 °C | 1.36E-5 1/K | ||
500.0 °C | 1.4E-5 1/K | ||
600.0 °C | 1.44E-5 1/K | ||
Max service temperature, long | -60 - 0 °C | ||
Melting point | 1382 - 1529 °C | Typical for Chromium Molybdenum Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 460 - 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 41 - 44 W/(m·K) | |
100.0 °C | 42.7 W/(m·K) | ||
200.0 °C | 42.8 W/(m·K) | ||
300.0 °C | 41.6 W/(m·K) | ||
400.0 °C | 39.9 W/(m·K) | ||
500.0 °C | 37.8 W/(m·K) | ||
600.0 °C | 35.6 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 11.4 mm²/s | |
100.0 °C | 11 mm²/s | ||
200.0 °C | 10.3 mm²/s | ||
300.0 °C | 9.5 mm²/s | ||
400.0 °C | 8.5 mm²/s | ||
500.0 °C | 7.3 mm²/s | ||
600.0 °C | 6 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.8E-7 - 2.54E-7 Ω·m |
100.0 °C | 3E-7 Ω·m | |
200.0 °C | 3.69E-7 Ω·m | |
300.0 °C | 4.51E-7 Ω·m | |
400.0 °C | 5.45E-7 Ω·m | |
500.0 °C | 6.54E-7 Ω·m | |
600.0 °C | 7.78E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.19 - 0.24 % |
Chromium | 0.7 - 1 % |
Manganese | 0.7 - 1 % |
Molybdenum | 0.4 - 0.5 % |
Phosphorus | 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.02 - 0.035 % |
Metal
- DIN 17210 Grade 15CrNi6 Steel – Cold Shearing (+S) for High‑Strength Applications
- 17CrNiMo6 Steel (DIN 17210) – Cold‑Shear +S Treatment for Heavy‑Duty Use
- DIN 17200 Grade 28CrS4: Cold‑Sheared Steel for High‑Load Automotive Parts (+S)
- DIN 17200 Grade 25CrMo4 Cold‑Sheared (+S) Steel – High Strength & Ductility for Automotive & Machinery
- DIN 17200 Grade 37Cr4 Steel – Cold‑Sheared, High‑Performance for Vehicle and Engine Components
- DIN 17200 Grade 37CrS4 – Cold Sheared & Heat‑Treated for Superior Performance
- DIN 17200 Grade 38Cr2 Steel – Cold‑Sheared, Superior Strength & Durability
- DIN 17200 Grade 46Cr2 – Cold‑Sheared Steel with Superior Strength for Automotive & Machinery Applications
- DIN 17200 Grade 28Cr4 – Cold‑Shear Treated Steel for High‑Load Automotive Parts
- DIN 17200 Grade 25CrMoS4 - Cold-Sheared with Enhanced Strength (S)