EN 10083-2 Grade C50 Steel – Cold‑Sheared and Treated for High‑Strength Applications

Steel C50 is suitable for components of higher strength and wear resistance demands in vehicle manufacturing, engine and machine engineering (e.g. shafts, hubs). Lowest working temperature -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

255 [-]

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

20.0 °C

81 GPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 - 52 W/(m·K)

100.0 °C

43.4 - 50.6 W/(m·K)

200.0 °C

43.2 - 48.1 W/(m·K)

300.0 °C

41.4 - 45.7 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.47 - 0.55 %

Chromium

0.4 %

Copper

0.3 %

Manganese

0.6 - 0.9 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.05 %

Silicon

0.1 - 0.4 %

Sulfur

0.045 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10269 Grade 42CrMo4 Steel – Cold Shear (+S) for High-Performance Automotive & Machinery Components
    2. EN 10269 Grade 21CrMoV5-7 Cold‑Sheared Steel for High‑Temperature Fasteners
    3. EN 10269 Grade 25CrMo4 – Cold Shear Treated Steel for Superior Strength and Durability
    4. EN 10083-1 Grade C30E Steel – Cold Shear Treatment (+S)
    5. EN 10083-1 Grade C30R Steel – Cold‑Sheared (+S) for Automotive & Machine Engineering
    6. EN 10083-2 Grade C30 Steel – Cold‑Sheared & Surface‑Treated for Automotive & Industrial Use
    7. EN 10083‑1 Grade 38CrS2 – Cold‑Shear Treated Steel for High‑Strength Applications
    8. EN 10083-1 Grade 46CrS2 – Cold Shearing Treated Steel for High-Strength Applications (+S)
    9. DIN 17200 Grade C50 Steel: Cold‑Sheared +S Treatment for Superior Strength
    10. EN 10083-2 Grade C25 Steel - Cold-Sheared +S Treatment for Vehicle & Machine Engineering