EN 10269 Grade 42CrMo4 Steel – Cold Shear (+S) for High-Performance Automotive & Machinery Components

Steel 42CrMo4 is suitable for high-stress components (also large forged parts) in vehicle, engine and machine engineering with high wear resistance and very favorable core properties ( e.g. crankshafts, pinions, balance shafts). The steel shows a high resistivity to static and dynamic loading. Lowest working temperature -40 °C Further application for mounting elements at increased and lower temperatures.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 - 7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

255 [-]

Poisson's ratio

20.0 °C

0.28 [-]

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.11E-5 - 1.21E-5 1/K

200.0 °C

1.21E-5 - 1.27E-5 1/K

300.0 °C

1.29E-5 - 1.32E-5 1/K

400.0 °C

1.35E-5 - 1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-40 - 0 °C

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.38 - 0.45 %

Chromium

0.9 - 1.2 %

Manganese

0.6 - 0.9 %

Molybdenum

0.15 - 0.3 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10269 Grade 21CrMoV5-7 Cold‑Sheared Steel for High‑Temperature Fasteners
    2. EN 10269 Grade 25CrMo4 – Cold Shear Treated Steel for Superior Strength and Durability
    3. EN 10083-1 Grade C30E Steel – Cold Shear Treatment (+S)
    4. EN 10083-1 Grade C30R Steel – Cold‑Sheared (+S) for Automotive & Machine Engineering
    5. EN 10083-2 Grade C30 Steel – Cold‑Sheared & Surface‑Treated for Automotive & Industrial Use
    6. EN 10083‑1 Grade 38CrS2 – Cold‑Shear Treated Steel for High‑Strength Applications
    7. EN 10083-1 Grade 46CrS2 – Cold Shearing Treated Steel for High-Strength Applications (+S)
    8. EN 10083-2 Grade C50 Steel – Cold‑Sheared and Treated for High‑Strength Applications
    9. EN 10083-1 Grade C25E – Cold Shearing Treated Steel (+S) for High-Performance Applications
    10. EN 10083-1 Grade C25R: Cold-Shear Treated Steel for Automotive & Machine Engineering