EN 10269 Grade 21CrMoV5-7 Cold‑Sheared Steel for High‑Temperature Fasteners

High-temperature steel for screws and nuts. Max. application temperature: 540 °C Further application for mounting elements at increased temperatures.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.84 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

211 - 212 GPa

100.0 °C

204 - 207 GPa

200.0 °C

196 - 199 GPa

300.0 °C

186 - 192 GPa

400.0 °C

177 - 184 GPa

500.0 °C

164 - 175 GPa

600.0 °C

127 - 164 GPa

Hardness, Brinell

20.0 °C

255 [-]

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Chromium Molybdenum Steel

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.11E-5 - 1.21E-5 1/K

200.0 °C

1.21E-5 - 1.27E-5 1/K

300.0 °C

1.29E-5 - 1.32E-5 1/K

400.0 °C

1.35E-5 - 1.36E-5 1/K

500.0 °C

1.39E-5 - 1.4E-5 1/K

600.0 °C

1.41E-5 - 1.44E-5 1/K

Max service temperature, long

0 - 540 °C

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

33 - 34.6 W/(m·K)

100.0 °C

36.9 W/(m·K)

200.0 °C

37.3 W/(m·K)

300.0 °C

36.9 W/(m·K)

400.0 °C

35.8 W/(m·K)

500.0 °C

34.4 W/(m·K)

600.0 °C

32.9 W/(m·K)

Thermal diffusivity

20.0 °C

9.6 mm²/s

100.0 °C

9.5 mm²/s

200.0 °C

9 mm²/s

300.0 °C

8.4 mm²/s

400.0 °C

7.6 mm²/s

500.0 °C

6.6 mm²/s

600.0 °C

5.5 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

3.01E-7 Ω·m

100.0 °C

3.47E-7 Ω·m

200.0 °C

4.23E-7 Ω·m

300.0 °C

5.09E-7 Ω·m

400.0 °C

6.08E-7 Ω·m

500.0 °C

7.19E-7 Ω·m

600.0 °C

8.43E-7 Ω·m

Chemical properties

PropertyValue

Aluminium

0.03 %

Carbon

0.17 - 0.25 %

Chromium

1.2 - 1.5 %

Manganese

0.4 - 0.8 %

Molybdenum

0.55 - 0.8 %

Nickel

0.6 %

Phosphorus

0.03 %

Silicon

0.4 %

Sulfur

0.03 %

Vanadium

0.2 - 0.35 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10269 Grade 42CrMo4 Steel – Cold Shear (+S) for High-Performance Automotive & Machinery Components
    2. EN 10269 Grade 25CrMo4 – Cold Shear Treated Steel for Superior Strength and Durability
    3. EN 10083-1 Grade C30E Steel – Cold Shear Treatment (+S)
    4. EN 10083-1 Grade C30R Steel – Cold‑Sheared (+S) for Automotive & Machine Engineering
    5. EN 10083-2 Grade C30 Steel – Cold‑Sheared & Surface‑Treated for Automotive & Industrial Use
    6. EN 10083‑1 Grade 38CrS2 – Cold‑Shear Treated Steel for High‑Strength Applications
    7. EN 10083-1 Grade 46CrS2 – Cold Shearing Treated Steel for High-Strength Applications (+S)
    8. EN 10083-2 Grade C50 Steel – Cold‑Sheared and Treated for High‑Strength Applications
    9. EN 10083-1 Grade C25E – Cold Shearing Treated Steel (+S) for High-Performance Applications
    10. EN 10083-1 Grade C25R: Cold-Shear Treated Steel for Automotive & Machine Engineering