DIN 17200 Grade 37CrS4 – Cold Sheared & Heat‑Treated for Superior Performance
Steel 37 CrS 4 is suitable for mean loaded parts of mean heat-treatment sections and enhanced workability in vehicle manufacturing, engine and machine engineering (e.g. gear wheels, transmission shafts, axles). Lowest application temp. -25 °C.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.83 - 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa |
20.0 °C | 210 - 212 GPa | |
100.0 °C | 205 - 207 GPa | |
200.0 °C | 195 - 199 GPa | |
300.0 °C | 185 - 192 GPa | |
400.0 °C | 175 - 184 GPa | |
500.0 °C | 175 GPa | |
600.0 °C | 164 GPa | |
Hardness, Brinell | 20.0 °C | 255 [-] |
Poisson's ratio | 20.0 °C | 0.28 [-] |
Shear modulus | 20.0 °C | 81 GPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.05E-5 1/K | |
20.0 °C | 1.15E-5 1/K | ||
100.0 °C | 1.11E-5 - 1.21E-5 1/K | ||
200.0 °C | 1.21E-5 - 1.27E-5 1/K | ||
300.0 °C | 1.29E-5 - 1.32E-5 1/K | ||
400.0 °C | 1.35E-5 - 1.36E-5 1/K | ||
500.0 °C | 1.4E-5 1/K | ||
600.0 °C | 1.44E-5 1/K | ||
Max service temperature, long | -25 - 0 °C | ||
Melting point | 1382 - 1529 °C | Typical for Chromium Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 460 - 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 45.1 - 46 W/(m·K) | |
100.0 °C | 45.1 W/(m·K) | ||
200.0 °C | 44.1 W/(m·K) | ||
300.0 °C | 41.9 W/(m·K) | ||
400.0 °C | 39.4 W/(m·K) | ||
500.0 °C | 36.9 W/(m·K) | ||
600.0 °C | 34.4 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 12.5 mm²/s | |
100.0 °C | 11.6 mm²/s | ||
200.0 °C | 10.6 mm²/s | ||
300.0 °C | 9.5 mm²/s | ||
400.0 °C | 8.4 mm²/s | ||
500.0 °C | 7.1 mm²/s | ||
600.0 °C | 5.8 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.9E-7 - 2.31E-7 Ω·m |
100.0 °C | 2.84E-7 Ω·m | |
200.0 °C | 3.58E-7 Ω·m | |
300.0 °C | 4.48E-7 Ω·m | |
400.0 °C | 5.52E-7 Ω·m | |
500.0 °C | 6.71E-7 Ω·m | |
600.0 °C | 8.06E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.34 - 0.41 % |
Chromium | 0.9 - 1.2 % |
Manganese | 0.6 - 0.9 % |
Phosphorus | 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.02 - 0.035 % |
Metal
- DIN 17200 Grade 28CrS4: Cold‑Sheared Steel for High‑Load Automotive Parts (+S)
- DIN 17200 Grade 25CrMo4 Cold‑Sheared (+S) Steel – High Strength & Ductility for Automotive & Machinery
- DIN 17200 Grade 37Cr4 Steel – Cold‑Sheared, High‑Performance for Vehicle and Engine Components
- DIN 17200 Grade 38Cr2 Steel – Cold‑Sheared, Superior Strength & Durability
- DIN 17200 Grade 46Cr2 – Cold‑Sheared Steel with Superior Strength for Automotive & Machinery Applications
- DIN 17200 Grade 28Cr4 – Cold‑Shear Treated Steel for High‑Load Automotive Parts
- DIN 17200 Grade 25CrMoS4 - Cold-Sheared with Enhanced Strength (S)
- DIN 17200 Grade 28Mn6 Steel – Cold Shear (+S) for Automotive & Machine Applications
- DIN 17200 Grade 34CrMoS4 – Cold Shear Treatment (+S) for High-Performance Automotive Components
- DIN 17200 Grade 34CrS4 – Cold Shear Treated Steel for High-Performance Applications