DIN 17850 Ti2 1/2 Hard Titanium – Superior Strength, Corrosion Resistance & Excellent Weldability
DIN Ti2 titanium is the second of four commercially unalloyed titanium grades. It has a moderate strength as well as excellent welding properties. The material is known for its good resistance to oxidation and corrosion.
Quantity: 300 EURAdditional services: Project based stainless steel packages for long, flat and tubular products. Implementing specs, approving mills and productions outfits, planning production finished and pre material routes. Making sure delivery is on time. Forgings, centrifugal casting, HIP products. Sourcing of materialHEMPEL SPECIAL METALS
MANUFACTURER, PROCESSOR AND DISTRIBUTOR
Information and services
Quantity: € 250Additional services: Project business and tailor made products; material consultancyProperties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20.0 °C | 4.505 g/cm³ | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 110.0 GPa | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | |
200.0 °C | 97.0 GPa | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | ||
400.0 °C | 82.0 GPa | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | ||
Poisson's ratio | 0.361 [-] | Typical for Pure Titanium | ||||
Shear modulus | 46.0 GPa | Typical for Pure Titanium | ||||
Tensile strength | 20.0 °C | 550.0 MPa | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 8.400000000000001e-06 - 8.599999999999999e-06 1/K | Typical for Pure Titanium | ||||
Melting point | 1670.0 °C | Typical for Pure Titanium | ||||
Specific heat capacity | 20.0 °C | 520.0 J/(kg·K) | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | |
200.0 °C | 570.0 J/(kg·K) | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | ||
400.0 °C | 630.0 J/(kg·K) | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | ||
Thermal conductivity | 20.0 °C | 22.6 W/(m·K) | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | |
200.0 °C | 20.9 W/(m·K) | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | ||
400.0 °C | 19.3 W/(m·K) | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical resistivity | 20.0 °C | 4.8e-07 Ω·m | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
200.0 °C | 8e-07 Ω·m | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire | |
400.0 °C | 1.14e-06 Ω·m | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Carbon | 0.06 | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Hydrogen | 0.013 | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Iron | 0.2 | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Nitrogen | 0.05 | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Oxygen | 0.18 | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Titanium | 99.1 % | 1/2 Hard | DIN 17850, WL 3.7034-1, VdTÜV WB 230-1, VdTÜV WB 230-2, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860 | Wire |
Metal
- JIS H4001 Grade 3004 Aluminium – ½ Hard Condition for Optimal Performance
- DIN 17741 NiMn1 1/2 Hard – Premium Nickel-Manganese Alloy
- High-Performance Ti2 Titanium Grade for Welding Applications
- DIN 17850 Grade Ti3 ½ Hard Titanium – High Strength & Corrosion Resistance
- DIN 17850 Ti-4 Titanium – 1/2 Hard Grade for Superior Strength
- DIN 17740 Ni99.6 1/2 Hard – Premium Corrosion-Resistant Nickel Alloy
- JIS G3141 SPCD 1/2 Hard Steel: Detailed Material Properties
- JIS G3141 Grade SPCE 1/2 Hard – Technical Specifications
- JIS G3141 Grade SPCC 1/2 Hard - Premium Low‑Carbon Steel for Structural Use
- DIN Ti1 Titanium – Softest Grade with Superior Ductility, Corrosion & Welding Performance