DIN 1725-1 Grade 3.0915 H24 – High‑Strength AlFeSi Alloy for Precision Forming

The alloy AlFeSi is alloyed for increasing the strength increase with Fe and Si. The material belongs to the nature-hard aluminum materials. A strength increase can be achieved only by cold forming. The alloy AlFeSi is very well cold and warm formable and has a good thermal and relatively good electrical conductivity. The material is particularly suitable for deep-drawing. It is well solderable. The material is to be oxidized well anodically, i.e. a shining clean surface develops. It is standardised as sheet metal or strip (DIN 1788 and DIN 1745). Application: for screw-type caps, for menu bowls, for light containers, bottle caps, cover containers and other form packing, for metal goods, like trim, decorated tiles, flexible pipes, various deep-drawing products, for heat exchangers and radiator fins

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.71 g/cm³	H24	EN 573-3, EN 485, EN 541, EN 546, EN 683
	20.0 °C	2.71 g/cm³	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus		70.0 GPa	H24	EN 573-3, EN 485, EN 541, EN 546, EN 683
Elongation		2.0 %	H24	EN 573-3, EN 541, EN 546		A50
		3.0 %	H24	EN 573-3, EN 485, EN 546		A50
		4.0 %	H24	EN 573-3, EN 485, EN 546, EN 683		A50
		5.0 %	H24	EN 573-3, EN 485, EN 546, EN 683		A50
		6.0 %	H24	EN 573-3, EN 485, EN 683		A50
		7.0 %	H24	EN 573-3, EN 485		A50
	20.0 °C	4.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	5.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	7.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Hardness, Brinell		40.0 [-]	H24	EN 573-3, EN 485
	20.0 °C	40.0 [-]	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 8000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 8000 Series Aluminium
Tensile strength		110.0 - 165.0 MPa	H24	EN 573-3, EN 546, EN 683
		120.0 - 160.0 MPa	H24	EN 573-3, EN 541
		125.0 - 165.0 MPa	H24	EN 573-3, EN 485
	20.0 °C	130.0 - 170.0 MPa	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	20 °C	2.35e-05 1/K	H24	EN 573-3, EN 485, EN 541, EN 546, EN 683
	100 °C	2.35e-05 1/K	H24	EN 573-3, EN 485, EN 541, EN 546, EN 683
Melting point		640.0 - 655.0 °C	H24	EN 573-3, EN 485, EN 541, EN 546, EN 683
Specific heat capacity		920.0 J/(kg·K)				Typical for Wrought 8000 Series Aluminium
Thermal conductivity	20.0 °C	210.0 - 220.0 W/(m·K)	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity	20.0 °C	34000000.0 - 35000000.0 S/m	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Electrical resistivity		2.86e-08 - 2.94e-08 Ω·m	H24	EN 573-3, EN 485, EN 541, EN 546, EN 683

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.1 %	H24	EN 573-3, EN 485, EN 541, EN 546, EN 683
Copper	0.1 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Iron	0.5 - 1.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Magnesium	0.1 %	H24	EN 573-3, EN 485, EN 541, EN 546, EN 683
Manganese	0.1 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Silicon	0.4 - 0.8 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat
Titanium	0.05	H24	DIN 1725-1, EN 573-3, EN 573-4	Flat
Zinc	0.1 %	H24	DIN 1725-1, EN 573-3, EN 573-4, EN 485, EN 541, EN 546, EN 683	Flat