DIN 1725-1 Grade 3.0915 H28 – High‑Strength AlFeSi Alloy for Deep‑Drawing and Anodizing

The alloy AlFeSi is alloyed for increasing the strength increase with Fe and Si. The material belongs to the nature-hard aluminum materials. A strength increase can be achieved only by cold forming. The alloy AlFeSi is very well cold and warm formable and has a good thermal and relatively good electrical conductivity. The material is particularly suitable for deep-drawing. It is well solderable. The material is to be oxidized well anodically, i.e. a shining clean surface develops. It is standardised as sheet metal or strip (DIN 1788 and DIN 1745). Application: for screw-type caps, for menu bowls, for light containers, bottle caps, cover containers and other form packing, for metal goods, like trim, decorated tiles, flexible pipes, various deep-drawing products, for heat exchangers and radiator fins

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20.0 °C	2.71 g/cm³	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus		69.0 - 72.0 GPa				Typical for Wrought 8000 Series Aluminium
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 8000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 8000 Series Aluminium
Tensile strength	20.0 °C	170.0 - 210.0 MPa	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion		1.9e-05 - 2.1e-05 1/K				Typical for Wrought 8000 Series Aluminium
Melting point		645.0 - 655.0 °C				Typical for Wrought 8000 Series Aluminium
Specific heat capacity		920.0 J/(kg·K)				Typical for Wrought 8000 Series Aluminium
Thermal conductivity	20.0 °C	210.0 - 220.0 W/(m·K)	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Electrical conductivity	20.0 °C	34000000.0 - 35000000.0 S/m	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat
Electrical resistivity		2.8e-08 - 3.5e-08 Ω·m				Typical for Wrought 8000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Copper	0.1	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat
Iron	0.5 - 1.0 %	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat
Manganese	0.1	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat
Silicon	0.4 - 0.8 %	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat
Titanium	0.05	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat
Zinc	0.1	H28	DIN 1725-1, EN 573-3, EN 573-4	Flat

AA Standard Grade 5010 H28: Comprehensive Mechanical Properties & Specifications EN 573-3 Grade 3.3316 F – Key Properties & Standards for 5000 Series Aluminium