DIN 1652-3 Grade 20MoCrS4: Cold Drawn, Turned & Soft Annealed – Superior Wear Resistance & Mechanical Performance
The steel 20 MoCrS 4 is used for wear loaded parts in the vehicle and mechanical engineering with medium core strength, better machinability, high toughness and high fatigue strength (e.g. gears, shafts, axles). The lowest application amounts to -60 °C, the best application up to 60 mm nominal size.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.83 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa | |
20.0 °C | 212 GPa | ||
100.0 °C | 207 GPa | ||
200.0 °C | 199 GPa | ||
300.0 °C | 192 GPa | ||
400.0 °C | 184 GPa | ||
500.0 °C | 175 GPa | ||
600.0 °C | 164 GPa | ||
Hardness, Brinell | 20.0 °C | 207 [-] | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Chromium Molybdenum Steel |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.05E-5 1/K | |
20.0 °C | 1.15E-5 1/K | ||
100.0 °C | 1.21E-5 1/K | ||
200.0 °C | 1.27E-5 1/K | ||
300.0 °C | 1.32E-5 1/K | ||
400.0 °C | 1.36E-5 1/K | ||
500.0 °C | 1.4E-5 1/K | ||
600.0 °C | 1.44E-5 1/K | ||
Max service temperature, long | -60 - 0 °C | ||
Melting point | 1382 - 1529 °C | Typical for Chromium Molybdenum Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 41 W/(m·K) | |
100.0 °C | 42.7 W/(m·K) | ||
200.0 °C | 42.8 W/(m·K) | ||
300.0 °C | 41.6 W/(m·K) | ||
400.0 °C | 39.9 W/(m·K) | ||
500.0 °C | 37.8 W/(m·K) | ||
600.0 °C | 35.6 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 11.4 mm²/s | |
100.0 °C | 11 mm²/s | ||
200.0 °C | 10.3 mm²/s | ||
300.0 °C | 9.5 mm²/s | ||
400.0 °C | 8.5 mm²/s | ||
500.0 °C | 7.3 mm²/s | ||
600.0 °C | 6 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 2.54E-7 Ω·m |
100.0 °C | 3E-7 Ω·m | |
200.0 °C | 3.69E-7 Ω·m | |
300.0 °C | 4.51E-7 Ω·m | |
400.0 °C | 5.45E-7 Ω·m | |
500.0 °C | 6.54E-7 Ω·m | |
600.0 °C | 7.78E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.17 - 0.22 % |
Chromium | 0.3 - 0.6 % |
Manganese | 0.7 - 1 % |
Molybdenum | 0.4 - 0.5 % |
Phosphorus | 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.02 - 0.035 % |
Metal
- DIN 1652-3 Grade 20MoCr4 – Premium Cold-Drawn, Turned, and Soft-Annealed Steel for High-Performance Applications
- DIN 1652-3 Grade 22CrMoS3-5: Cold-Drawn or Turned, Soft-Annealed Steel for High-Performance Automotive & Mechanical Applications
- DIN 1652-3 Grade 17CrNiMo6: Cold‑Drawn, Turned & Soft‑Annealed High‑Strength Steel
- DIN 1652-3 Grade 20Cr4 Steel – Cold Drawn/Turned & Soft Annealed for High-Wear Applications
- DIN 1652-3 Grade 20CrS4: High‑Wear, High‑Machinability Steel for Automotive and Mechanical Applications
- DIN 1652-3 Grade 20MnCrS5: Premium Cold‑Drawn & Turned Steel, Soft‑Annealed for High‑Performance Applications
- DIN 1652-3 Grade 15CrNi6 – Cold Drawn or Turned & Soft Annealed Steel for High‑Strength Automotive and Mechanical Applications
- DIN 1652-3 Grade 16MnCr5 Steel – Cold Drawn or Turned, Soft Annealed for High-Strength Applications
- DIN 1652‑3 Grade 16MnCrS5 – Cold‑Drawn, Turned, Soft‑Annealed Steel for Automotive Gears, Shafts & Steering
- DIN 1652-3 Grade 17Cr3: Cold-Drawn, Turned, Soft-Annealed Steel for High-Wear Applications