High-Performance 16MnCr5 Steel: Spheroidized Carbides, Cold-Drawn, Annealed, Ideal for Automotive Screws & Gears

The cold-upsettable steel 16 MnCr 5 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for bevel gears, gear shafts, valve spring plates (for example in case-hardened condition).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

62 %

Tensile strength

20.0 °C

530 - 550 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Melting point

1382 - 1529 °C

Typical for Chromium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.9 W/(m·K)

100.0 °C

46.4 W/(m·K)

200.0 °C

45.6 W/(m·K)

300.0 °C

43.5 W/(m·K)

400.0 °C

40.9 W/(m·K)

500.0 °C

38.2 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

12.7 mm²/s

100.0 °C

12 mm²/s

200.0 °C

11 mm²/s

300.0 °C

9.9 mm²/s

400.0 °C

8.7 mm²/s

500.0 °C

7.3 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.27E-7 Ω·m

100.0 °C

2.76E-7 Ω·m

200.0 °C

3.46E-7 Ω·m

300.0 °C

4.31E-7 Ω·m

400.0 °C

5.32E-7 Ω·m

500.0 °C

6.48E-7 Ω·m

600.0 °C

7.81E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.14 - 0.19 %

Chromium

0.8 - 1.1 %

Manganese

1 - 1.3 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10263‑4 Grade 38Cr2 Steel: Cold‑Drawn, Annealed, Spheroidized Carbides & Slight Skin Pass
    2. EN 10263-4 Grade 41Cr4 Steel: Cold‑Drawn, Annealed for Spheroidized Carbides & Enhanced Surface Quality
    3. EN 10263-4 Grade 42CrMo4: Cold-Drawn, Annealed Steel with Spheroidized Carbides
    4. EN 10263-4 Grade 46Cr2 Steel – Cold Drawn, Annealed for Spheroidized Carbides with Light Skin Pass
    5. EN 10263-4 Grade Cq35 Steel – Cold Drawn, Annealed, Spheroidized Carbides, Skin-Passed
    6. EN 10263-3 Grade 17Cr3 Cold‑Drawn Steel – Annealed for Spheroidized Carbides & Skin‑Passed Finish
    7. EN 10263-3 Grade 20MoCr4 Steel: Cold‑Drawn, Annealed for Spheroidized Carbides, Slightly Skin‑Passed
    8. EN 10263-3 Grade 15CrNi6 Cold-Drawn, Annealed Steel with Spheroidized Carbides – Ideal for Automotive Fasteners
    9. EN 10263-3 Grade 21NiCrMo2: Cold-Drawn, Annealed Steel with Spheroidized Carbides and Light Skin Passivation
    10. Grade Cq15 Cold-Drawn Steel – Spheroidized Carbides, Annealed, Slightly Skin-Passed