High-Performance TZM Pickled Sheet – Titanium‑Zirconium‑Molybdenum Alloy

Molybdenum is transformed into TZM (Titanium-Zirconium-Molybdenum) by using small quantities of tiny, extremely fine carbides. TZM is stronger than pure molybdenum and possesses a higher recrystallization temperature and better creep resistance.

Properties

General

Property	Temperature	Value
Density	23.0 °C	10.1 g/cm³

Dimension

Property	Value
Length	600 mm
Thickness	10 - 20 mm
Width	400 mm
Dimensions	Available dimensions (width x length x thickness, mm x mm x mm): 400 x 600 x 10; 400 x 600 x 20

Mechanical

Property	Temperature	Value
Elongation	23.0 °C	10 %
Hardness, Vickers	23.0 °C	220 - 320 [-]
Tensile strength	23.0 °C	650 MPa
Yield strength Rp0.2	23.0 °C	600 MPa

Chemical properties

Property	Value
Aluminium	1E-4 %
Cadmium	1E-4 %
Chromium	3E-4 %
Copper	2E-4 %
Iron	5E-4 %
Molybdenum	balance
Nickel	1E-4 %
Nitrogen	5E-4 %
Oxygen	0.01 %
Potassium	6E-4 %
Silicon	2E-4 %
Titanium	0.4 - 0.55 %
Tungsten	0.02 %
Zirconium	0.06 - 0.12 %

Technological properties

Property
Application areas	TZM is used in high-temperature applications involving demanding mechanical loads, for example in forging tools or as rotating anodes in X-ray tubes. The recommended temperatures of use are between 700 and 1400 °C.

DIN 17864 TiAl6Zr5Mo0.5Si: Artificially Aged High‑Temperature Alloy AMPCO® 26: Premium Hard-Grade Aluminium Bronze Castings