Amstrong® 355MC: High-Strength, High-Ductility Steel for Weight-Saving Applications

Amstrong® 355MC characterised by high ductility, controlled internal purity, fine grain structure and low carbon content. On request, Amstrong® may be delivered with an improved surface finish on black hot-rolled product called MASC (Micro Adhesive Scale). Contact our commercial teams for further information.

It combines:

• Outstanding mechanical properties
  • High strength
  • Toughness
  • Fatigue resistance
• Good formability
• Good weldability

  
  

  With its high strength, it is an excellent choice when weight-saving is a priority, and is frequently used to replace structural steels.

  Properties

  General

  Property	Value	Comment
  Carbon equivalent (CEV)	0.32 [-]	max.

  Dimension

  Property	Value
  Dimensions	*Pickled products with thicknesses up to 15 mm may be delivered after prior agreement: please contact us. Please feel free to check the figure on the right side of the material page for more details.

  Mechanical

  Property	Temperature	Value	Comment
  Charpy impact energy	-20 °C	40 J	min. | for thickness 6-16 mm
  Elongation		21 %	min. | for thickness < 3 mm | Transverse, A80
  		22 %	min. | for thickness < 3 mm, A80
  		24 %	min. A5.65√So | for thickness 3-16 mm | Transverse
  		25 %	min. A5.65√So | for thickness 3-16 mm
  Tensile strength		430 - 520 MPa	for thickness < 16 mm
  		440 - 530 MPa	for thickness < 16 mm | Transverse
  Yield strength		355 - 435 MPa	for thickness < 16 mm
  		380 - 460 MPa	for thickness < 16 mm | Transverse

  Chemical properties

  Property	Value	Comment
  Aluminium	0.015 %	min.
  Carbon	0.1 %	max.
  Manganese	1.4 %	max.
  Niobium	0.065 %	max.
  Phosphorus	0.02 %	max.
  Silicon	0.03 %	max.
  Sulfur	0.015 %	max.
  Titanium	0.15 %	max.
  Vanadium	0.2 %	max.

  Technological properties

  Property
  Application areas	High strength Amstrong® steels are used in a wide range of applications in transport (earth movers, trailers, agricultural and railroad machinery etc), profiling (racks etc) and building (cranes, safety barriers, light poles etc). Significant weight reductions can be achieved by using Amstrong® steels, especially for cranes and heavy vehicle trailers, thus allowing a larger payload.
  Chemical composition	The chemical properties given are based on cast analysis data.
  Coating	Galvanisation: Class 1 Suitability for hot-dip zinc coating is defined as per the requirements of EN ISO 14713-2 Table 1 and NFA 35-503.
  Other	Toughness guarantee at -40°C: on request

  
  