EN 12513 Grade G-X 260 NiCr 4/2 Steel: High Wear Resistance & Moderate Impact Stress
G-X 260 NiCr 4 2, has a high wear resistance, usable at moderate impact stress.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.7 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 169 - 183 GPa | |
Hardness, Brinell | 20.0 °C | 430 - 690 [-] | |
Hardness, Vickers | 20.0 °C | 450 - 750 [-] | |
Poisson's ratio | 23.0 °C | 0.27 [-] | Typical for Cast Iron |
Shear modulus | 23.0 °C | 41 GPa | Typical for Cast Iron |
Tensile strength | 20.0 °C | 320 - 390 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.5E-5 1/K | Typical for White Cast Iron |
Melting point | 1209 °C | Typical for White Cast Iron | |
Specific heat capacity | 23.0 °C | 460 J/(kg·K) | Typical for White Cast Iron |
Thermal conductivity | 20.0 °C | 14 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 8E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Carbon | 2.6 - 2.9 % |
Chromium | 1.4 - 2.4 % |
Manganese | 0.3 - 0.7 % |
Molybdenum | 0.5 % |
Nickel | 3.3 - 5 % |
Silicon | 0.2 - 0.8 % |
Metal
- ASTM A514 Grade F Low-Carbon Steel – Key Properties & Applications
- EN 1652 CuCo1Ni1Be TH – High-Performance Copper Alloy for Industrial Applications
- EN 12163 CuZr TH Grade – High Strength Low‑Alloy Copper Alloy
- EN 12163 Grade CuBe2 M: High-Performance Hardenable Copper Alloy
- EN 12163 Grade CuZn10 M – High-Strength, Corrosion-Resistant Copper Alloy
- EN 10305-5 Grade St 33 Welded Precision Steel Tubes
- EN 12513 G-X 300 CrNiSi 9/5/2: High-Performance Wear-Resistant Cast Iron
- EN 12513 G-X 330 NiCr 4.2 – Premium High‑Wear Resistance Steel
- BS 3100 Grade A1 Steel Specifications & Properties
- WL 3.2364 T5: Superior Weldable Cast Alloy for High-Integrity Applications