EN 10277-4 Grade 16MnCrS5: Soft-Annealed & Peeled Steel for High-Strength Vehicle & Machine Parts

Steel 16MnCrS5 is suitable for parts of higher dimension in vehicle and machine engineering that require higher core strength and enhanced workability (e.g. gear wheels, shafts, steering parts). Lowest application temperature -25°C, most favorable application area up to 50 mm nominal size. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

207 GPa

200.0 °C

188 - 199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

207 [-]

Poisson's ratio

20.0 °C

0.28 [-]

25.0 °C

0.26 - 0.29 [-]

Shear modulus

20.0 °C

81 GPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.1E-5 - 1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-25 - 0 °C

Melting point

1382 - 1529 °C

Typical for Chromium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

42 - 45.9 W/(m·K)

100.0 °C

39.8 - 46.4 W/(m·K)

200.0 °C

37.7 - 45.6 W/(m·K)

300.0 °C

43.5 W/(m·K)

400.0 °C

40.9 W/(m·K)

500.0 °C

38.2 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

12.7 mm²/s

100.0 °C

12 mm²/s

200.0 °C

11 mm²/s

300.0 °C

9.9 mm²/s

400.0 °C

8.7 mm²/s

500.0 °C

7.3 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.6E-7 - 2.27E-7 Ω·m

100.0 °C

2.76E-7 Ω·m

200.0 °C

3.46E-7 Ω·m

300.0 °C

4.31E-7 Ω·m

400.0 °C

5.32E-7 Ω·m

500.0 °C

6.48E-7 Ω·m

600.0 °C

7.81E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.14 - 0.19 %

Chromium

0.8 - 1.1 %

Manganese

1 - 1.3 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.02 - 0.04 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277‑5 42CrMoS4 Soft‑Annealed & Peeled Steel – High Strength & Wear Resistance
    2. EN 10277-4 Grade 20MnCrS5 Steel – Soft‑Annealed, Peeled, and Ready for High‑Performance Applications
    3. EN 10277-5 Grade 51CrV4 Soft‑Annealed & Peeled Steel (+A+SH) – Superior Wear Resistance for High‑Load Applications
    4. EN 10277‑5 25CrMoS4 Soft‑Annealed & Peeled Steel – Premium High‑Strength Performance
    5. EN 10277-5 Grade 34CrNiMo6 Soft Annealed & Peeled Steel – High‑Load, High‑Temperature Performance
    6. EN 10277-5 Grade 34CrS4: Soft Annealed & Peeled Steel for Vehicle & Engine Applications
    7. EN 10277-4 Grade 20NiCrMoS2-2: Soft‑Annealed & Peeled Steel for Automotive & Machinery Applications
    8. EN 10277-4 Grade C10R: Soft-Annealed, Peeled Steel Bars (+A+SH)
    9. EN 10277-4 Grade C16R Soft‑Annealed & Peeled Steel Bars – Premium Low‑Carbon Steel
    10. EN 10277-4 Grade C15R Soft Annealed & Peeled Steel – Ideal for Wear‑Resistant Vehicle & Machine Parts