EN 10277-5 Grade 34CrNiMo6 Soft Annealed & Peeled Steel – High‑Load, High‑Temperature Performance

Steel 25CrMoS4 is suitable for high loaded parts (also heavy forged parts) of high heat-treatment sections as well as favorable ductility qualities in aircraft, heavy vehicle and machine engineering (e.g. propellershafts, connecting rods, transmission shafts). Lowest application temperature -40°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

248 [-]

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Nickel Chromium Molybdenum Steel

Shear modulus

20.0 °C

81 GPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.11E-5 - 1.21E-5 1/K

200.0 °C

1.21E-5 - 1.27E-5 1/K

300.0 °C

1.29E-5 - 1.32E-5 1/K

400.0 °C

1.35E-5 - 1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-40 - 0 °C

Melting point

1382 - 1529 °C

Typical for Nickel Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

33.7 - 42 W/(m·K)

100.0 °C

36.2 - 50.3 W/(m·K)

200.0 °C

37.8 - 49 W/(m·K)

300.0 °C

37.2 - 47.8 W/(m·K)

400.0 °C

35.7 W/(m·K)

500.0 °C

34 W/(m·K)

600.0 °C

32 W/(m·K)

Thermal diffusivity

20.0 °C

9.4 mm²/s

100.0 °C

9.4 mm²/s

200.0 °C

9.2 mm²/s

300.0 °C

8.5 mm²/s

400.0 °C

7.6 mm²/s

500.0 °C

6.6 mm²/s

600.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.9E-7 - 3.09E-7 Ω·m

100.0 °C

3.54E-7 Ω·m

200.0 °C

4.18E-7 Ω·m

300.0 °C

5.05E-7 Ω·m

400.0 °C

6.09E-7 Ω·m

500.0 °C

7.27E-7 Ω·m

600.0 °C

8.67E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.3 - 0.38 %

Chromium

1.3 - 1.7 %

Manganese

0.5 - 0.8 %

Molybdenum

0.15 - 0.3 %

Nickel

1.3 - 1.7 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277‑5 42CrMoS4 Soft‑Annealed & Peeled Steel – High Strength & Wear Resistance
    2. EN 10277-4 Grade 20MnCrS5 Steel – Soft‑Annealed, Peeled, and Ready for High‑Performance Applications
    3. EN 10277-5 Grade 34CrNiMo6 – Cold Drawn/Turned, Soft Annealed Steel for High-Load Applications
    4. EN 10277-5 Grade 51CrV4 Soft‑Annealed & Peeled Steel (+A+SH) – Superior Wear Resistance for High‑Load Applications
    5. EN 10277‑5 25CrMoS4 Soft‑Annealed & Peeled Steel – Premium High‑Strength Performance
    6. EN 10277-5 Grade 34CrS4: Soft Annealed & Peeled Steel for Vehicle & Engine Applications
    7. EN 10277-5 Grade 41CrS4 Soft Annealed & Peeled Steel for Automotive & Machinery Parts
    8. EN 10277-4 Grade 16MnCrS5: Soft-Annealed & Peeled Steel for High-Strength Vehicle & Machine Parts
    9. EN 10277-4 Grade 20NiCrMoS2-2: Soft‑Annealed & Peeled Steel for Automotive & Machinery Applications
    10. EN 10277-4 Grade C15R Soft Annealed & Peeled Steel – Ideal for Wear‑Resistant Vehicle & Machine Parts