EN 10277‑5 25CrMoS4 Soft‑Annealed & Peeled Steel – Premium High‑Strength Performance
Steel 25CrMoS4 is suitable for parts of high strength and ductility demands and mean and higher heat-treatment sections as well as enhanced workability in vehicle, engine and machine engineering (e.g. crankshafts, steering knuckles, pinions). Lowest application temperature -40°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.83 - 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa | |
20.0 °C | 210 - 212 GPa | ||
100.0 °C | 205 - 207 GPa | ||
200.0 °C | 195 - 199 GPa | ||
300.0 °C | 185 - 192 GPa | ||
400.0 °C | 184 GPa | ||
500.0 °C | 175 GPa | ||
600.0 °C | 164 GPa | ||
Hardness, Brinell | 20.0 °C | 212 [-] | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Chromium Molybdenum Steel |
Shear modulus | 20.0 °C | 81 GPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.05E-5 1/K | |
20.0 °C | 1.15E-5 1/K | ||
100.0 °C | 1.11E-5 - 1.21E-5 1/K | ||
200.0 °C | 1.21E-5 - 1.27E-5 1/K | ||
300.0 °C | 1.29E-5 - 1.32E-5 1/K | ||
400.0 °C | 1.35E-5 - 1.36E-5 1/K | ||
500.0 °C | 1.4E-5 1/K | ||
600.0 °C | 1.44E-5 1/K | ||
Max service temperature, long | -40 - 0 °C | ||
Melting point | 1382 - 1529 °C | Typical for Chromium Molybdenum Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 460 - 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 41 - 50 W/(m·K) | |
100.0 °C | 42.7 W/(m·K) | ||
200.0 °C | 42.8 W/(m·K) | ||
300.0 °C | 41.6 W/(m·K) | ||
400.0 °C | 39.9 W/(m·K) | ||
500.0 °C | 37.8 W/(m·K) | ||
600.0 °C | 35.6 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 11.4 mm²/s | |
100.0 °C | 11 mm²/s | ||
200.0 °C | 10.3 mm²/s | ||
300.0 °C | 9.5 mm²/s | ||
400.0 °C | 8.5 mm²/s | ||
500.0 °C | 7.3 mm²/s | ||
600.0 °C | 6 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.8E-7 - 2.54E-7 Ω·m |
100.0 °C | 3E-7 Ω·m | |
200.0 °C | 3.69E-7 Ω·m | |
300.0 °C | 4.51E-7 Ω·m | |
400.0 °C | 5.45E-7 Ω·m | |
500.0 °C | 6.54E-7 Ω·m | |
600.0 °C | 7.78E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.22 - 0.29 % |
Chromium | 0.9 - 1.2 % |
Manganese | 0.6 - 0.9 % |
Molybdenum | 0.15 - 0.3 % |
Phosphorus | 0.03 - 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.02 - 0.04 % |
Metal
- EN 10277‑5 42CrMoS4 Soft‑Annealed & Peeled Steel – High Strength & Wear Resistance
- EN 10277-4 Grade 20MnCrS5 Steel – Soft‑Annealed, Peeled, and Ready for High‑Performance Applications
- EN 10277-5 Grade 25CrMoS4 – Cold‑Drawn, Turned & Soft‑Annealed High‑Strength Steel
- EN 10277-5 Grade 51CrV4 Soft‑Annealed & Peeled Steel (+A+SH) – Superior Wear Resistance for High‑Load Applications
- EN 10277-5 Grade 34CrNiMo6 Soft Annealed & Peeled Steel – High‑Load, High‑Temperature Performance
- EN 10277-5 Grade 34CrS4: Soft Annealed & Peeled Steel for Vehicle & Engine Applications
- EN 10277-5 Grade 41CrS4 Soft Annealed & Peeled Steel for Automotive & Machinery Parts
- EN 10277-4 Grade 16MnCrS5: Soft-Annealed & Peeled Steel for High-Strength Vehicle & Machine Parts
- EN 10277-4 Grade 20NiCrMoS2-2: Soft‑Annealed & Peeled Steel for Automotive & Machinery Applications
- EN 10277-4 Grade C15R Soft Annealed & Peeled Steel – Ideal for Wear‑Resistant Vehicle & Machine Parts