EN 10277-4 Grade 20NiCrMoS2-2: Soft‑Annealed & Peeled Steel for Automotive & Machinery Applications
Steel 20NiCrMoS-2 is suitable for parts in vehicle and machine engineering, that are wear loaded at mean core strength, high ductility and fatigue resistance (e.g. gear wheels, shafts, axles). The show an enhanced workability. Lowest application temperature -60°C, most favorable application area up to 60 mm nominal size. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.84 - 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa |
20.0 °C | 205 - 212.78 GPa | |
100.0 °C | 207 GPa | |
200.0 °C | 188 - 199 GPa | |
300.0 °C | 192 GPa | |
400.0 °C | 184 GPa | |
500.0 °C | 175 GPa | |
600.0 °C | 164 GPa | |
Hardness, Brinell | 20.0 °C | 212 [-] |
Poisson's ratio | 20.0 °C | 0.29 [-] |
Shear modulus | 20.0 °C | 79 - 82.8 GPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.05E-5 1/K | |
20.0 °C | 1.15E-5 1/K | ||
100.0 °C | 1.1E-5 - 1.21E-5 1/K | ||
200.0 °C | 1.27E-5 1/K | ||
300.0 °C | 1.32E-5 1/K | ||
400.0 °C | 1.36E-5 1/K | ||
500.0 °C | 1.4E-5 1/K | ||
600.0 °C | 1.44E-5 1/K | ||
Max service temperature, long | -60 - 0 °C | ||
Melting point | 1382 - 1529 °C | Typical for Nickel Chromium Molybdenum Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 460 - 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 44 - 46.3 W/(m·K) | |
100.0 °C | 47.1 W/(m·K) | ||
200.0 °C | 46.2 W/(m·K) | ||
300.0 °C | 44.1 W/(m·K) | ||
400.0 °C | 41.3 W/(m·K) | ||
500.0 °C | 38.6 W/(m·K) | ||
600.0 °C | 35.9 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 12.8 mm²/s | |
100.0 °C | 12.1 mm²/s | ||
200.0 °C | 11.1 mm²/s | ||
300.0 °C | 10 mm²/s | ||
400.0 °C | 8.8 mm²/s | ||
500.0 °C | 7.4 mm²/s | ||
600.0 °C | 4.7 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.6E-7 - 2.25E-7 Ω·m |
100.0 °C | 2.72E-7 Ω·m | |
200.0 °C | 3.42E-7 Ω·m | |
300.0 °C | 4.26E-7 Ω·m | |
400.0 °C | 5.26E-7 Ω·m | |
500.0 °C | 6.4E-7 Ω·m | |
600.0 °C | 7.73E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.17 - 0.23 % |
Chromium | 0.35 - 0.7 % |
Manganese | 0.65 - 0.95 % |
Molybdenum | 0.15 - 0.25 % |
Nickel | 0.4 - 0.7 % |
Phosphorus | 0.03 - 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.02 - 0.04 % |
Metal
- EN 10277‑5 42CrMoS4 Soft‑Annealed & Peeled Steel – High Strength & Wear Resistance
- EN 10277-4 Grade 20MnCrS5 Steel – Soft‑Annealed, Peeled, and Ready for High‑Performance Applications
- EN 10277-5 Grade 51CrV4 Soft‑Annealed & Peeled Steel (+A+SH) – Superior Wear Resistance for High‑Load Applications
- EN 10277‑5 25CrMoS4 Soft‑Annealed & Peeled Steel – Premium High‑Strength Performance
- EN 10277-5 Grade 34CrNiMo6 Soft Annealed & Peeled Steel – High‑Load, High‑Temperature Performance
- EN 10277-5 Grade 34CrS4: Soft Annealed & Peeled Steel for Vehicle & Engine Applications
- EN 10277-4 Grade 16MnCrS5: Soft-Annealed & Peeled Steel for High-Strength Vehicle & Machine Parts
- EN 10277-4 Grade C10R: Soft-Annealed, Peeled Steel Bars (+A+SH)
- EN 10277-4 Grade C16R Soft‑Annealed & Peeled Steel Bars – Premium Low‑Carbon Steel
- EN 10277-4 Grade C15R Soft Annealed & Peeled Steel – Ideal for Wear‑Resistant Vehicle & Machine Parts