DIN 17103 TStE 500: High‑Strength Steel for Extreme Conditions
The fine grained steel TStE 500 is used for welded constructions of different kind like pressure vessels, stationary or mobile storage tanks, high pressure lines, bridge and support constructions etc. The application temperature of the tough at subzero temperatures grade amounts to -50 °C.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20 °C | 7.84 g/cm³ | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | -100 °C | 217 GPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
20 °C | 212 GPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
100 °C | 207 GPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
200 °C | 199 GPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
300 °C | 192 GPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
400 °C | 184 GPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
500 °C | 175 GPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
600 °C | 164 GPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
Elongation | 20 °C | 16 % | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
Poisson's ratio | 0.3 [-] | Typical for Steel | ||||
Tensile strength | 20 °C | 570 - 780 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
20 °C | 570 - 770 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 570 - 760 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 570 - 750 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 570 - 740 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 580 - 780 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 580 - 770 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 580 - 760 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 580 - 750 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 580 - 740 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 590 - 780 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 590 - 770 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 590 - 760 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 590 - 750 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 590 - 740 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 600 - 780 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 600 - 770 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 600 - 760 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 600 - 750 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 600 - 740 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 610 - 780 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 610 - 770 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 610 - 760 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 610 - 750 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 610 - 740 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
Yield strength | 20 °C | 410 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
20 °C | 420 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 430 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 440 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 450 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 460 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 470 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 480 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | ||
20 °C | 500 MPa | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | -100 °C | 1.05e-05 1/K | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
20 °C | 1.15e-05 1/K | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
100 °C | 1.21e-05 1/K | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
200 °C | 1.27e-05 1/K | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
300 °C | 1.32e-05 1/K | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
400 °C | 1.36e-05 1/K | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
500 °C | 1.4e-05 1/K | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
600 °C | 1.44e-05 1/K | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
Specific heat capacity | -100 °C | 423 J/(kg·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
20 °C | 461 J/(kg·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
100 °C | 479 J/(kg·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
200 °C | 499 J/(kg·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
300 °C | 517 J/(kg·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
400 °C | 536 J/(kg·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
500 °C | 558 J/(kg·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
600 °C | 587 J/(kg·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
Thermal conductivity | -100 °C | 34.7 W/(m·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
20 °C | 39.7 W/(m·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
100 °C | 40.9 W/(m·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
200 °C | 41 W/(m·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
300 °C | 39.9 W/(m·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
400 °C | 38.2 W/(m·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
500 °C | 36.1 W/(m·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
600 °C | 33.8 W/(m·K) | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
Thermal diffusivity | -100 °C | 11.9 mm²/s | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
20 °C | 11 mm²/s | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
100 °C | 10.5 mm²/s | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
200 °C | 9.9 mm²/s | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
300 °C | 9.1 mm²/s | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
400 °C | 8.1 mm²/s | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
500 °C | 6.9 mm²/s | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
600 °C | 5.7 mm²/s | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical resistivity | -100 °C | 1.97e-07 Ω·m | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
20 °C | 2.62e-07 Ω·m | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
100 °C | 3.13e-07 Ω·m | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
200 °C | 3.85e-07 Ω·m | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
300 °C | 4.7e-07 Ω·m | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
400 °C | 5.69e-07 Ω·m | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
500 °C | 6.85e-07 Ω·m | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar | |
600 °C | 8.2e-07 Ω·m | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 0.02 % | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Carbon | 0.21 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Chromium | 0.3 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Copper | 0.2 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Manganese | 1 - 1.7 % | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Molybdenum | 0.1 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Nickel | 1 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Niobium | 0.05 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Nitrogen | 0.02 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Phosphorus | 0.03 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Silicon | 0.1 - 0.6 % | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Sulfur | 0.025 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Vanadium | 0.22 | normalized or normalized formed (+N) | DIN 17102, EN 10025-1, EN 10025-3, EN 10028-1, EN 10028-3, DIN 17103 | Sheet, Strip, Bar |
Metal
- DIN 17103 Grade StE 500: Normalized or Normalized Formed Steel (+N) – Key Properties & Applications
- DIN 17103 WStE 460 Steel: Normalized & Normalized Formed (+N) for High-Temperature Applications
- DIN 17103 WStE 420: High‑Temperature Normalized Steel for Robust Welded Constructions
- DIN 17103 WStE 500 – Normalized & Normalized Formed Steel for High‑Temperature Applications
- DIN 17125 Grade TStE 460 – Normalized or Normalized‑Formed Steel for High‑Temperature Applications
- DIN 17103: Grade StE 285 – Normalized or Normalized-Formed Steel (+N) Specifications
- WStE 285 Steel (DIN 17103) – Normalized or Normalized Formed (N): Properties & Applications
- DIN 17103 WStE 355: High-Temperature Grade Steel – Normalized or Normalized +N
- DIN 17125 Grade TStE 355 – Normalized or Normalized Formed Steel Tubes (+N)
- DIN 17103 Grade TStE 285: Normalized or Normalized Formed Steel for Low‑Temperature Applications