DIN 17230 44Cr2 Quenched & Tempered Steel – High‑Performance Anti‑Friction Bearing Material

44 Cr 2 is an anti-friction bearing steel that can be refined and induction hardened. In the Jominy test it reaches surface hardnesses of approximately 62 HRC. It is used for discs and anti-friction bearing parts of larger dimensions.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

12 - 15 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Steel

Reduction of area

20.0 °C

35 - 45 %

Tensile strength

20.0 °C

650 - 1100 MPa

Yield strength

20.0 °C

400 - 650 MPa

Thermal

PropertyTemperatureValue

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 W/(m·K)

100.0 °C

43.4 W/(m·K)

200.0 °C

43.2 W/(m·K)

300.0 °C

41.4 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.42 - 0.48 %

Chromium

0.4 - 0.6 %

Copper

0.3 %

Manganese

0.5 - 0.8 %

Phosphorus

0.03 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17350 Grade 102Cr6 Tool Steel – Quenched & Tempered (QT) for High‑Performance Cutting Tools
    2. DIN 17350 Grade 21MnCr5: High-Performance Quenched & Tempered Steel for Superior Hardness
    3. DIN 17480 X85CrMoV18-2 Quenched & Tempered Steel – Technical Specifications
    4. DIN 17480 X45CrSi9-3 Steel – Quenched & Tempered (QT) Specification
    5. DIN 17230 Grade 43CrMo4 Quenched & Tempered Steel – Superior Bearing Performance
    6. DIN 17230 Grade 48CrMo4: Quenched & Tempered Anti-Friction Steel
    7. DIN 17230 Cf54 Quenched & Tempered Steel – Premium Anti‑Friction Bearing Material
    8. DIN 17240 Grade C35 Quenched & Tempered Steel – High-Temperature Creep Resistance
    9. DIN 17240 Grade Ck 35 – Quenched & Tempered Steel for High-Temperature Bolt & Nut Applications
    10. DIN 17240 Grade Cq 35 Quenched & Tempered Steel – High-Temperature Creep-Resistant for Bolts & Nuts