DIN 17230 Grade 43CrMo4 Quenched & Tempered Steel – Superior Bearing Performance

43 CrMo 4 is an anti-friction bearing steel that can be refined and induction hardened. In the Jominy test it reaches surface hardnesses of approximately 61 HRC. It is used for discs and anti-friction bearing parts of larger dimensions.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 - 7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

10 - 14 %

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

40 - 55 %

Tensile strength

20.0 °C

750 - 1300 MPa

Yield strength

20.0 °C

500 - 900 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.4 - 0.46 %

Chromium

0.9 - 1.2 %

Copper

0.3 %

Manganese

0.6 - 0.9 %

Molybdenum

0.15 - 0.35 %

Phosphorus

0.03 %

Sulfur

0.4 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17350 Grade 102Cr6 Tool Steel – Quenched & Tempered (QT) for High‑Performance Cutting Tools
    2. DIN 17350 Grade 21MnCr5: High-Performance Quenched & Tempered Steel for Superior Hardness
    3. DIN 17480 X85CrMoV18-2 Quenched & Tempered Steel – Technical Specifications
    4. DIN 17480 X45CrSi9-3 Steel – Quenched & Tempered (QT) Specification
    5. DIN 17230 44Cr2 Quenched & Tempered Steel – High‑Performance Anti‑Friction Bearing Material
    6. DIN 17230 Grade 48CrMo4: Quenched & Tempered Anti-Friction Steel
    7. DIN 17230 Cf54 Quenched & Tempered Steel – Premium Anti‑Friction Bearing Material
    8. DIN 17240 Grade C35 Quenched & Tempered Steel – High-Temperature Creep Resistance
    9. DIN 17240 Grade Ck 35 – Quenched & Tempered Steel for High-Temperature Bolt & Nut Applications
    10. DIN 17240 Grade Cq 35 Quenched & Tempered Steel – High-Temperature Creep-Resistant for Bolts & Nuts