DIN 17440 X30Cr13: Quenched & Tempered Steel – Superior Cutting Tools & Bearings

Properties: - in hardened state resistant to water and steam - in annealed or high tempered state corrosion resitance is not sufficient - application in hardened state with fine grounded or polished surface Application: - for manufacturing cutting tools (knife blades, scissors, surgical instruments) - spherical for bearings, wear resistant control elements and parts for pumps, spring, plunger, srews

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.7 - 7.71 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

220 - 222 GPa

100.0 °C

216 - 218 GPa

200.0 °C

209 - 212 GPa

300.0 °C

201 - 205 GPa

400.0 °C

192 - 197 GPa

500.0 °C

183 GPa

600.0 °C

174 GPa

Elongation

20.0 °C

11 %

Poisson's ratio

23.0 °C

0.3 [-]

Typical for Martensitic Stainless Steel

Shear modulus

23.0 °C

77 GPa

Typical for Martensitic Stainless Steel

Tensile strength

20.0 °C

800 - 1000 MPa

Yield strength Rp0.2

20.0 °C

600 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

1.02E-5 1/K

100.0 °C

1.05E-5 1/K

200.0 °C

1.09E-5 - 1.1E-5 1/K

300.0 °C

1.13E-5 - 1.15E-5 1/K

400.0 °C

1.16E-5 - 1.2E-5 1/K

500.0 °C

1.2E-5 1/K

600.0 °C

1.22E-5 1/K

Max service temperature, long

0 - 400 °C

Melting point

1370 - 1530 °C

Typical for Martensitic Stainless Steel

Specific heat capacity

20.0 °C

439 - 460 J/(kg·K)

100.0 °C

474 J/(kg·K)

200.0 °C

498 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

538 J/(kg·K)

500.0 °C

564 J/(kg·K)

600.0 °C

598 J/(kg·K)

Thermal conductivity

20.0 °C

24.6 - 30 W/(m·K)

100.0 °C

24.7 W/(m·K)

200.0 °C

25 W/(m·K)

300.0 °C

25.2 W/(m·K)

400.0 °C

25.5 W/(m·K)

500.0 °C

25.8 W/(m·K)

600.0 °C

26 W/(m·K)

Thermal diffusivity

20.0 °C

7.3 mm²/s

100.0 °C

6.4 mm²/s

200.0 °C

6.1 mm²/s

300.0 °C

5.8 mm²/s

400.0 °C

5.4 mm²/s

500.0 °C

4.8 mm²/s

600.0 °C

4.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

5.87E-7 - 6.5E-7 Ω·m

100.0 °C

6.55E-7 Ω·m

200.0 °C

7.38E-7 Ω·m

300.0 °C

8.19E-7 Ω·m

400.0 °C

8.96E-7 Ω·m

500.0 °C

9.7E-7 Ω·m

600.0 °C

1.04E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.26 - 0.35 %

Chromium

12 - 14 %

Manganese

1 - 1.5 %

Phosphorus

0.04 - 0.05 %

Silicon

1 %

Sulfur

0.015 - 0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10250-4 X30Cr13 Quenched & Tempered Steel – Ideal for Cutting Tools & High‑Wear Parts
    2. DIN 17440 X12CrMoS17 Steel – Quenched & Tempered Grade for High-Performance Applications
    3. DIN 17440 Grade X14CrMoS17 – Quenched & Tempered Stainless Steel for Pressure Vessels & Structural Components
    4. DIN 17440: X12Cr13 Quenched & Tempered Steel for High-Pressure Applications
    5. DIN 17240 Grade C35 Quenched & Tempered Steel – High-Temperature Creep Resistance
    6. DIN 17440 Grade X15Cr13: Quenched & Tempered Steel for High-Performance Applications
    7. DIN 17440 X10Cr13 – Premium Quenched & Tempered Steel for 550 °C Applications
    8. DIN 17440 X20CrNi17-2: Premium Quenched & Tempered Steel for High-Performance Use
    9. X17CrNi16-2 Grade – DIN 17440 Quenched & Tempered (QT) Steel for High-Performance Applications
    10. DIN 17440 Grade X20Cr13 Quenched & Tempered (+QT) – High‑Performance Stainless Steel for Industrial Applications