DIN 1654-5 X2CrNiN18-10: Premium Cold‑Drawn, Quenched Steel for High‑Temperature Chemical Applications

X 2 CrNi 18 10 is an austenitic CrNi steel which, due to the added nitrogen alloy, possesses an increased yield strength which also persist in higher temperatures. It is suitable for the chemical equipment construction because of its resistance to nitric acid. The steel is well suited for cold-forming and can undergo high-gloss polishing. It is used for screws, nuts and molded parts at temperatures from -270 up to 400 degrees C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.93 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

206 GPa

20.0 °C

196 GPa

100.0 °C

190 - 194 GPa

200.0 °C

182 - 186 GPa

300.0 °C

174 - 179 GPa

400.0 °C

166 - 172 GPa

500.0 °C

158 - 165 GPa

600.0 °C

150 GPa

700.0 °C

142 GPa

800.0 °C

134 GPa

900.0 °C

127 GPa

1000.0 °C

120 GPa

Poisson's ratio

20.0 °C

0.3 [-]

Typical for Austenitic Stainless Steel

Reduction of area

20.0 °C

55 %

Tensile strength

20.0 °C

790 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.49E-5 1/K

20.0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200.0 °C

1.7E-5 - 1.72E-5 1/K

300.0 °C

1.7E-5 - 1.77E-5 1/K

400.0 °C

1.8E-5 - 1.81E-5 1/K

500.0 °C

1.8E-5 - 1.84E-5 1/K

600.0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800.0 °C

1.94E-5 1/K

900.0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

Max service temperature, long

-270 - 400 °C

Melting point

1375 - 1450 °C

Typical for Austenitic Stainless Steel

Specific heat capacity

-100.0 °C

440 J/(kg·K)

20.0 °C

472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200.0 °C

503 J/(kg·K)

300.0 °C

512 J/(kg·K)

400.0 °C

520 J/(kg·K)

500.0 °C

530 J/(kg·K)

600.0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800.0 °C

559 J/(kg·K)

900.0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

Thermal conductivity

20.0 °C

14.3 W/(m·K)

100.0 °C

15.8 W/(m·K)

200.0 °C

17.5 W/(m·K)

300.0 °C

19 W/(m·K)

400.0 °C

20.5 W/(m·K)

500.0 °C

21.9 W/(m·K)

600.0 °C

23.3 W/(m·K)

700.0 °C

24.6 W/(m·K)

800.0 °C

26 W/(m·K)

900.0 °C

27.4 W/(m·K)

1000.0 °C

28.8 W/(m·K)

Thermal diffusivity

20.0 °C

3.8 mm²/s

100.0 °C

4 mm²/s

200.0 °C

4.2 mm²/s

300.0 °C

4.6 mm²/s

400.0 °C

4.8 mm²/s

500.0 °C

4.9 mm²/s

600.0 °C

5 mm²/s

700.0 °C

5.3 mm²/s

800.0 °C

5.6 mm²/s

900.0 °C

5.9 mm²/s

1000.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

7.1E-7 Ω·m

100.0 °C

7.76E-7 Ω·m

200.0 °C

8.49E-7 Ω·m

300.0 °C

9.14E-7 Ω·m

400.0 °C

9.71E-7 Ω·m

500.0 °C

1.02E-6 Ω·m

600.0 °C

1.07E-6 Ω·m

700.0 °C

1.1E-6 Ω·m

800.0 °C

1.14E-6 Ω·m

900.0 °C

1.17E-6 Ω·m

1000.0 °C

1.19E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.03 %

Chromium

17 - 19 %

Manganese

2 %

Nickel

8.5 - 11.5 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1654-5 Grade X3CrNiCu18-9 Stainless Steel – Cold‑Drawn, Quenched & Slightly Skinned for Superior Performance
    2. X5CrNi18-12 Stainless Steel – DIN 1654-5 Grade, Cold‑Drawn, Quenched & Skin‑Passed
    3. DIN 1654‑5 X6CrNiMoTi 17‑12‑2: Cold‑Drawn, Quenched & Finely Surface‑Processed Steel
    4. DIN 1654-5 Grade X5CrNiMo17-12-2: Premium Cold-Drawn & Quenched Stainless Steel
    5. DIN 1654-5 Grade X5CrNiMo17-12-2: Cold‑Drawn, Quenched, Lightly Skinned – Premium Stainless Steel for Chemical & Pharmaceutical Use
    6. DIN 1654-5 X6CrNiTi18-10 Cold-Drawn Stainless Steel – Superior Corrosion Resistance
    7. DIN 1654-5 Grade X2CrNi19-11: Cold-Drawn & Quenched Steel for High-Performance Applications
    8. DIN 1654-5 Grade X2CrNi19-11 Steel – Cold‑Drawn, Quenched & Skin‑Passed for High‑Performance Applications
    9. DIN 1654-5 Grade X2CrNiMoN17-13-3: Premium Cold-Drawn, Quenched, and Skin-Passed Stainless Steel
    10. DIN 1654-5 Grade X2CrNiN18-10 – Cold‑Drawn & Quenched Austenitic Stainless Steel