DIN 17851 TiAl5Fe2.5 Annealed – High Strength, Corrosion Resistance & Biocompatibility

Chemical composition: DIN 17851 With smaller cross sections, the alpha + beta alloy TiAl5Fe2.5 is hardenable up to 1300 N/mm^2. There are acceptable high temperature tensile strengths and creep strengths up to approximately 450 °C. The material shows excellent corrosion-resistance especially to oxidizing mediums. Application: Because of its compatibility to tissue, TiAl5Fe2.5 is applied as implant alloy in the medical technology, e.g. for hip and joint prostheses.

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20.0 °C	4.45 g/cm³	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	20.0 °C	116.0 GPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
Elongation	20.0 °C	8.0	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging	Transverse
	20.0 °C	8.0	Annealed	DIN 17862, DIN 17851, DIN 17864, DIN 17860	Rod
Hardness, Brinell	20.0 °C	310.0	Annealed	DIN 17862, DIN 17851, DIN 17864, DIN 17860	Rod
Reduction of area	20.0 °C	30.0 %	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging	Transverse
	20.0 °C	30.0 %	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
Tensile strength	20.0 °C	860.0 MPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging	Transverse
	20.0 °C	860.0 MPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
	20.0 °C	1020.0 MPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860
	100.0 °C	925.0 MPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860
	200.0 °C	840.0 MPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860
	300.0 °C	770.0 MPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860
	400.0 °C	715.0 MPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860
	500.0 °C	585.0 MPa	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860

Thermal

Property	Value	Comment
Coefficient of thermal expansion	7.699999999999999e-06 - 1e-05 1/K	Typical for Titanium Alpha Beta Alloy
Melting point	1500.0 - 1750.0 °C	Typical for Titanium Alpha Beta Alloy
Specific heat capacity	370.0 - 674.0 J/(kg·K)	Typical for Titanium Alpha Beta Alloy
Thermal conductivity	6.0 - 12.0 W/(m·K)	Typical for Titanium Alpha Beta Alloy

Chemical properties

Property	Value	Condition	Related Standards	Shape
Aluminium	4.5 - 5.5 %	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
Carbon	0.08	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
Hydrogen	0.015	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
Iron	2.0 - 3.0 %	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
Nitrogen	0.05	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
Oxygen	0.2	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod
Titanium	90.8 %	Annealed	DIN 17851, DIN 17864, DIN 17862, DIN 17860	Forging, Rod