DIN 17851 TiAl6V6Sn2 Annealed Alloy: Superior Strength & Corrosion Resistance for Aerospace

Chemical composition: DIN 17851 TiAl6V6Sn2 with the material number 3.7175 (see also TiAl6V6Sn2, material number 3.7174, according to the Werkstoff-Leistungsblatt der Deutschen Luftfahrt WL 3.7174) belongs to the hardenable alpha + beta-titanium alloys. It is similar to the 3.7164 or 3.7165 (TiAl6V4), yet the beta-phase is more stable and the material shows higher strength. It possesses good resistance to corrosion, it is well forgeable, and the long-term application temperature is approximately 350 °C. Processing properties: Formability: limited (cold forming), good (hot forming) Weldability: limited (embrittlement of the welding and heat affected zone by transformation hardening, electron-beam welding) (Werkstoff-Leistungsblatt der Deutschen Luftfahrt WL: material specification of the German aviation)

Properties

General

PropertyTemperatureValueConditionRelated StandardsShape

Density

20.0 °C

4.54 g/cm³

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Elastic modulus

20.0 °C

116.0 GPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

200.0 °C

108.0 GPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

400.0 °C

99.0 GPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Elongation

20.0 °C

6.0 %

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Plate

20.0 °C

7.0 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod

Transverse

20.0 °C

8.0 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate

Hardness, Brinell

20.0 °C

320.0

Annealed

DIN 17862, WL 3.7174-1, DIN 17851, DIN 17864, DIN 17860

Rod

Plane-Strain Fracture Toughnes

20.0 °C

46.1 - 54.8 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Plate

20.0 °C

46.1 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Plate

20.0 °C

54.8 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Plate

20.0 °C

62.7 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Rod, Forging

20.0 °C

62.7 - 71.9 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Rod, Forging

20.0 °C

62.7 - 70.8 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Rod, Forging

20.0 °C

70.8 - 71.9 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Rod, Forging

20.0 °C

70.8 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Rod, Forging

20.0 °C

71.9 MPa·√m

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Rod, Forging

Reduction of area

20.0 °C

15.0 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging

Transverse

20.0 °C

20.0 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate

Shear modulus

20.0 °C

45.0 GPa

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Forging, Plate, Rod, Flat

Tensile strength

20.0 °C

1000.0 MPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod

Transverse

20.0 °C

1000.0 MPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate

20.0 °C

1030.0 MPa

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Plate

20.0 °C

1070.0 MPa

Annealed

WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860

Flat

20.0 °C

1140.0 MPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

100.0 °C

1065.0 MPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

200.0 °C

990.0 MPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

300.0 °C

930.0 MPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

400.0 °C

900.0 MPa

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Thermal

PropertyTemperatureValueConditionRelated StandardsShapeComment

Coefficient of thermal expansion

7.699999999999999e-06 - 1e-05 1/K

Typical for Titanium Alpha Beta Alloy

Melting point

1500.0 - 1750.0 °C

Typical for Titanium Alpha Beta Alloy

Specific heat capacity

370.0 - 674.0 J/(kg·K)

Typical for Titanium Alpha Beta Alloy

Thermal conductivity

20.0 °C

6.5 W/(m·K)

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Electrical

PropertyTemperatureValueConditionRelated StandardsShape

Electrical resistivity

20.0 °C

1.57e-06 Ω·m

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Chemical properties

PropertyValueConditionRelated StandardsShape

Aluminium

5.0 - 6.0 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Carbon

0.05

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Copper

0.35 - 1.0 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Hydrogen

0.015

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod

Iron

0.35 - 1.0 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Nitrogen

0.04

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Oxygen

0.2

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Tin

1.5 - 2.5 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Titanium

82.8 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat

Vanadium

5.0 - 6.0 %

Annealed

DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Forging, Rod, Plate, Flat


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17442 X38CrMoV15 Soft-Annealed Stainless Steel – Superior Corrosion Resistance
    2. DIN 17210 Grade 21NiCrMo2 Soft Annealed Steel – Superior Wear Resistance & Fatigue Strength
    3. DIN 17210 Grade 20CrS4 Soft Annealed Steel: High Wear Resistance & Machinability
    4. DIN 17210 Grade 21NiCrMoS2 Soft Annealed Steel (+A) – High Performance for Wear-Resistant Applications
    5. DIN 17210 Grade 20Cr4 Soft‑Annealed Steel – High Wear Resistance for Automotive & Mechanical Applications
    6. DIN 17851 Ti1Pd Alloy: High Corrosion Resistance & Excellent Weldability
    7. DIN 17851 TiAl5Fe2.5 Annealed – High Strength, Corrosion Resistance & Biocompatibility
    8. DIN 17851 TiAl6V6Sn2 – Premium High-Strength, Corrosion-Resistant Titanium Alloy
    9. DIN 2391-2 St 30 Al Seamless Steel Tube – Soft Annealed, Grade A
    10. DIN 2391-2 St 30 Si Soft‑Annealed Tube – Grade A for Precision Construction