EN 10277-3 Grade 35SPb20 Cold-Drawn Steel – Premium Strength & Machinability
The free cutting case hardening steel 35SPb20 is used for bulk parts of mean strength, especially lower ductility demands in transversal direction compared to other C-steels (e.g. C35). Machinability enhancement is achieved by Pb-content. Application in car industry, apparatus, equipment and machine engineering (e.g. screws, nuts, small-size parts). As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 210 GPa | |
200.0 °C | 193 GPa | ||
300.0 °C | 185 GPa | ||
400.0 °C | 175 GPa | ||
Elongation | 20.0 °C | 6 - 9 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Medium Carbon Steel |
Shear modulus | 20.0 °C | 81 GPa | |
Tensile strength | 20.0 °C | 510 - 880 MPa | |
Yield strength Rp0.2 | 20.0 °C | 300 - 480 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.1E-5 1/K | |
200.0 °C | 1.18E-5 1/K | ||
400.0 °C | 1.32E-5 1/K | ||
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1380 - 1514 °C | Typical for Medium Carbon Steel | |
Specific heat capacity | 20.0 °C | 420 J/(kg·K) | |
100.0 °C | 490 J/(kg·K) | ||
200.0 °C | 530 J/(kg·K) | ||
400.0 °C | 610 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 49 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.2E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.32 - 0.39 % |
Lead | 0.15 - 0.35 % |
Manganese | 0.7 - 1.1 % |
Phosphorus | 0.06 % |
Silicon | 0.4 % |
Sulfur | 0.15 - 0.25 % |
Metal
- EN 10277-3 Grade 46SPb20 Cold Drawn Steel – High Strength, Low Ductility, Pb‑Enhanced Machinability
- EN 10277-3 Grade 35SPb20 Cold-Drawn Steel – Premium Strength & Machinability
- EN 10277-3 Grade 35S20 Cold Drawn Steel – High Strength & Ductility for Automotive & Machine Parts
- EN 10277-3 46S20 Cold-Drawn Steel – High Strength, Low Ductility for Automotive & Machinery Applications
- EN 10277-3 Grade 10SPb20 Cold-Drawn Steel – Uniform Properties & Enhanced Machinability
- EN 10277-3 Grade 11SMnPb30 Cold Drawn Steel – High Machinability & Low Cracking Sensitivity
- EN 10277-3 Grade 11SMnPb37 – Cold‑Drawn High‑Performance Free‑Cutting Steel
- EN 10277-3 Grade 10S20 Cold Drawn Steel – Superior Machinability & Ductility for Case-Hardened Parts
- EN 10277-3 Grade 11SMn30 Cold Drawn Steel – Superior Performance for Automotive and Industrial Applications
- EN 10277-3 Grade 11SMn37 Cold Drawn Steel – Premium Quality for Industrial Applications