EN 10263-4 Grade 41Cr4 Quenched & Tempered Steel – Optimal for Cold-Forming, High-Strength Screws & Ball Studs

The cold-upsettable steel 41 Cr 4 can be cold-formed with the suitable tools with a low to medium rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used for normed screws and screws manufactured according to drawings of strength class 8.8 in the thick dimension range of strength class 12.9 in the thin dimension range. Also used for high-strength parts manufactured according to drawings (ball studs).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

10 - 14 %

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

30 - 40 %

Tensile strength

20.0 °C

800 - 1200 MPa

Yield strength

20.0 °C

560 - 800 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Melting point

1382 - 1529 °C

Typical for Chromium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.38 - 0.45 %

Chromium

0.9 - 1.2 %

Manganese

0.6 - 0.9 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10263-4 Grade 37Cr4 Quenched & Tempered Steel – High Strength & Durability
    2. EN 10263-4 Grade 38Cr2 Quenched & Tempered Steel – Specifications & Applications
    3. EN 10263-4 Grade 42CrMo4 Quenched & Tempered Steel – High‑Strength, Cold‑Formable Grade 10.9/12.9
    4. EN 10263-4 Grade 46Cr2 Quenched & Tempered Steel: High-Strength, Precision-Engineered for Heavy-Duty Fasteners
    5. EN 10263-4 Grade 30CrNiMo8 Steel – Quenched & Tempered (QT) for High‑Strength Screws
    6. EN 10263-4 Grade 34Cr4 Quenched & Tempered Steel – High Strength & Formability
    7. EN 10263-4: Grade 34CrNiMo6 Quenched & Tempered Steel – High-Strength, Cold-Formable
    8. EN 10297-1 Grade 41Cr4 Quenched & Tempered Steel – Properties & Performance
    9. EN 10263-4 Grade 25CrMo4 Quenched & Tempered Steel – High Strength, Cold-Formable
    10. EN 10263-4 Grade 34CrMo4 Quenched & Tempered Steel – High Strength & Versatility