EN 10213 G17CrMo5-5: High-Performance Quenched & Tempered Steel for Turbines & Boiler Casings

Material G17CrMo5-5 is equivalent to trademark GS-17 CrMo 5 5 acc. to DIN17245-87. It is used at room temperature and increased temperatures for thick-walled castings, for turbines, pressure vessels and steam boilers, e.g. for casings, fittings and valve boxes.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

211 GPa

100.0 °C

204 GPa

200.0 °C

196 GPa

300.0 °C

186 GPa

400.0 °C

177 GPa

500.0 °C

164 GPa

600.0 °C

127 GPa

Elongation

20.0 °C

20 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Chromium Molybdenum Steel

Tensile strength

20.0 °C

490 - 690 MPa

Yield strength Rp0.2

20.0 °C

315 MPa

200.0 °C

250 MPa

300.0 °C

230 MPa

350.0 °C

215 MPa

400.0 °C

200 MPa

450.0 °C

190 MPa

500.0 °C

175 MPa

550.0 °C

160 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.18E-5 - 1.22E-5 1/K

200.0 °C

1.29E-5 1/K

300.0 °C

1.29E-5 - 1.34E-5 1/K

400.0 °C

1.39E-5 1/K

500.0 °C

1.37E-5 - 1.43E-5 1/K

600.0 °C

1.46E-5 1/K

Max service temperature, long

300 - 610 °C

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

20.0 °C

460 J/(kg·K)

Thermal conductivity

20.0 °C

50 W/(m·K)

50.0 °C

38.5 W/(m·K)

300.0 °C

46 W/(m·K)

400.0 °C

42 W/(m·K)

500.0 °C

38 W/(m·K)

600.0 °C

34 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.6E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.15 - 0.2 %

Chromium

1 - 1.5 %

Copper

0.3 %

Manganese

0.5 - 1 %

Molybdenum

0.45 - 0.65 %

Nickel

0.4 %

Phosphorus

0.02 %

Silicon

0.6 %

Sulfur

0.02 %

Vanadium

0.05 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
    2. EN 10213 Grade G17CrMo9-10 – Quenched & Tempered (QT) Steel for High-Temperature Applications
    3. EN 10213 Grade G20Mo5 Quenched & Tempered: Premium Steel for Turbine Applications
    4. EN 10213: GX4CrNi13-4 Martensitic Stainless Steel – Quenched & Tempered (+QT) – Key Properties
    5. EN 10213 GX4CrNiMo16-5-1: Premium Quenched & Tempered Steel for High-Performance Applications
    6. EN 10213 G17CrMoV5-10: High-Strength Quenched & Tempered Steel for Turbine Components
    7. EN 10213 GP280GH Steel – Quenched & Tempered (QT) – Superior Mechanical Properties
    8. EN 10213 Grade GX23CrMoV12-1: Quenched and Tempered Steel for High‑Temperature Applications
    9. EN 10213 GP240GH Quenched & Tempered Steel – High‑Temperature, Weldable Performance
    10. EN 10213 G17Mn5 Quenched & Tempered Steel – High-Performance Pressure Vessel Material