EN 10213 GP280GH Steel – Quenched & Tempered (QT) – Superior Mechanical Properties
Material GP280GH is applicated at room temperature and increased temperatures.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.8 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for High Carbon Steel |
Elongation | 20.0 °C | 22 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for High Carbon Steel |
Shear modulus | 23.0 °C | 81 GPa | Typical for High Carbon Steel |
Tensile strength | 20.0 °C | 480 - 640 MPa | |
Yield strength Rp0.2 | 20.0 °C | 280 MPa | |
100.0 °C | 250 MPa | ||
200.0 °C | 220 MPa | ||
300.0 °C | 190 MPa | ||
350.0 °C | 170 MPa | ||
400.0 °C | 160 MPa | ||
450.0 °C | 150 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.28E-5 1/K | |
300.0 °C | 1.36E-5 1/K | ||
500.0 °C | 1.45E-5 1/K | ||
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1289 - 1478 °C | Typical for High Carbon Steel | |
Specific heat capacity | 20.0 °C | 460 J/(kg·K) | |
Thermal conductivity | 50.0 °C | 45 W/(m·K) | |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.18 - 0.25 % |
Chromium | 0.3 % |
Copper | 0.3 % |
Manganese | 0.8 - 1.2 % |
Molybdenum | 0.12 % |
Nickel | 0.4 % |
Phosphorus | 0.03 % |
Silicon | 0.6 % |
Sulfur | 0.02 % |
Vanadium | 0.03 % |
Metal
- EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
- EN 10213 Grade G17CrMo9-10 – Quenched & Tempered (QT) Steel for High-Temperature Applications
- EN 10213 G17CrMo5-5: High-Performance Quenched & Tempered Steel for Turbines & Boiler Casings
- EN 10213 Grade G20Mo5 Quenched & Tempered: Premium Steel for Turbine Applications
- EN 10213: GX4CrNi13-4 Martensitic Stainless Steel – Quenched & Tempered (+QT) – Key Properties
- EN 10213 GX4CrNiMo16-5-1: Premium Quenched & Tempered Steel for High-Performance Applications
- EN 10213 G17CrMoV5-10: High-Strength Quenched & Tempered Steel for Turbine Components
- EN 10213 Grade GX23CrMoV12-1: Quenched and Tempered Steel for High‑Temperature Applications
- EN 10213 GP240GH Quenched & Tempered Steel – High‑Temperature, Weldable Performance
- EN 10213 G17Mn5 Quenched & Tempered Steel – High-Performance Pressure Vessel Material