EN 10213: GX4CrNi13-4 Martensitic Stainless Steel – Quenched & Tempered (+QT) – Key Properties
Material GX4CrNi13-4 is used at room temperature and incrased temperatures
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.7 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 220 GPa | Typical for Martensitic Stainless Steel |
Elongation | 20.0 °C | 15 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Martensitic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Martensitic Stainless Steel |
Tensile strength | 20.0 °C | 760 - 960 MPa | |
Yield strength Rp0.2 | 20.0 °C | 550 MPa | |
100.0 °C | 515 MPa | ||
200.0 °C | 485 MPa | ||
300.0 °C | 455 MPa | ||
350.0 °C | 440 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.05E-5 1/K | |
300.0 °C | 1.1E-5 1/K | ||
500.0 °C | 1.2E-5 1/K | ||
Melting point | 1370 - 1530 °C | Typical for Martensitic Stainless Steel | |
Specific heat capacity | 20.0 °C | 460 J/(kg·K) | |
Thermal conductivity | 50.0 °C | 26 W/(m·K) | |
100.0 °C | 27 W/(m·K) | ||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 6E-7 Ω·m | Typical for Martensitic Stainless Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.06 % |
Chromium | 12 - 13.5 % |
Copper | 0.3 % |
Manganese | 1 % |
Molybdenum | 0.7 % |
Nickel | 3.5 - 5 % |
Phosphorus | 0.04 % |
Silicon | 1 % |
Sulfur | 0.025 % |
Tin | 0.03 % |
Vanadium | 0.08 % |
Metal
- EN 10137-2 Grade S890QL – High-Strength Quenched & Tempered Steel for Heavy-Duty Applications
- EN 10213 Grade G17CrMo9-10 – Quenched & Tempered (QT) Steel for High-Temperature Applications
- EN 10213 G17CrMo5-5: High-Performance Quenched & Tempered Steel for Turbines & Boiler Casings
- EN 10213 Grade G20Mo5 Quenched & Tempered: Premium Steel for Turbine Applications
- EN 10213 GX4CrNiMo16-5-1: Premium Quenched & Tempered Steel for High-Performance Applications
- EN 10213 G17CrMoV5-10: High-Strength Quenched & Tempered Steel for Turbine Components
- EN 10213 GP280GH Steel – Quenched & Tempered (QT) – Superior Mechanical Properties
- EN 10213 Grade GX23CrMoV12-1: Quenched and Tempered Steel for High‑Temperature Applications
- EN 10213 GP240GH Quenched & Tempered Steel – High‑Temperature, Weldable Performance
- EN 10213 G17Mn5 Quenched & Tempered Steel – High-Performance Pressure Vessel Material