EN 10263-4 Grade 42CrMo4 Quenched & Tempered Steel – High‑Strength, Cold‑Formable Grade 10.9/12.9

The cold-upsettable steel 42 CrMo 4 can be cold-formed according to the usual forming methods on single-stage and multi-stage presses. Because of its high carbon content, only low to medium forming degrees are recommendable. It is used for screws of strength class 10.9 in the thick and of strength class 12.9 in the medium to thin dimension range.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

10 - 12 %

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

40 - 50 %

Tensile strength

20.0 °C

650 - 1300 MPa

Yield strength

20.0 °C

650 - 900 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.38 - 0.45 %

Chromium

0.9 - 1.2 %

Manganese

0.6 - 0.9 %

Molybdenum

0.15 - 0.3 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10132-3: 42CrMo4 Quenched & Tempered Alloy Steel – Premium Cold-Rolled Strips
    2. EN 10263-4 Grade 37Cr4 Quenched & Tempered Steel – High Strength & Durability
    3. EN 10263-4 Grade 38Cr2 Quenched & Tempered Steel – Specifications & Applications
    4. EN 10263-4 Grade 41Cr4 Quenched & Tempered Steel – Optimal for Cold-Forming, High-Strength Screws & Ball Studs
    5. EN 10263-4 Grade 46Cr2 Quenched & Tempered Steel: High-Strength, Precision-Engineered for Heavy-Duty Fasteners
    6. EN 10263-4 Grade 30CrNiMo8 Steel – Quenched & Tempered (QT) for High‑Strength Screws
    7. EN 10263-4 Grade 34Cr4 Quenched & Tempered Steel – High Strength & Formability
    8. EN 10263-4: Grade 34CrNiMo6 Quenched & Tempered Steel – High-Strength, Cold-Formable
    9. EN 10269 Grade 42CrMo4 Quenched & Tempered (QT) – High‑Performance Steel for Heavy‑Duty Applications
    10. EN 10263-4 Grade 25CrMo4 Quenched & Tempered Steel – High Strength, Cold-Formable