EN 10263-4 Grade Cq45 – Annealing for Spheroidized Carbides & Turning

The cold-upsettable steel Cq 45 can be cold-formed with a low to medium rate of forming according to the usual forming methods on single-stage and multi-stage presses. BEcause of its unfavourable processing properties, Cq 45 should be replaced with steel 35 B 2. It is used for normed screws of strength class 8.8 (in the lower dimension range) as well as for nuts of strength classes 8 and 10.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Reduction of area

20.0 °C

60 %

Shear modulus

23.0 °C

75 - 80 GPa

Typical for Carbon Steel

Tensile strength

20.0 °C

590 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 W/(m·K)

100.0 °C

43.4 W/(m·K)

200.0 °C

43.2 W/(m·K)

300.0 °C

41.4 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.42 - 0.5 %

Manganese

0.5 - 0.8 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10263-4 Grade 41Cr4 – Annealed for Spheroidized Carbides & Precision Turning
    2. EN 10263-4: Grade 42CrMo4 Steel – Annealed for Spheroidized Carbides and Precision Turning
    3. EN 10263-4 Grade 46Cr2: Annealed for Spheroidized Carbides & Precision Turning
    4. EN 10263-4 Grade 30CrNiMo8 Steel: Annealed for Spheroidized Carbides & Precision Turning
    5. EN 10263-4 Grade 34Cr4 Steel – Annealed with Spheroidized Carbides for Hexagonal Screws
    6. EN 10263-4 Grade 34CrNiMo6 – Annealed for Spheroidized Carbides, Ideal for High‑Strength Screws & Stress‑Critical Extrusions
    7. EN 10263-4 Grade 37Cr4: Annealed for Spheroidized Carbides and Precision Turning
    8. EN 10263‑4 Grade 38Cr2 – Annealed for Spheroidized Carbides & Precision Turning
    9. EN 10263-4 Grade 25CrMo4: Annealed for Spheroidized Carbides & Turned Components
    10. EN 10263-4 Grade 34CrMo4: Annealed for Spheroidized Carbides and Precision Turning