DIN 1654-5 Grade X10Cr13: Annealed for Spheroidized Carbides (+AC) – Ideal for Cold‑Forming

The steel X10Cr13 is well suited for cold-forming in the annealed condition. The strain hardening inclination is significantly lower than that of stainless austenitic steels and is about equal to that of a carbon steel. It is used for construction parts operating in water and steam, and for mild media in the food industry, predominantly in the tempered condition (screws and molded parts). Temperature of use: up to 550 degrees C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.73 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

20.0 °C

217 - 217.99 GPa

100.0 °C

213.2 - 215 GPa

200.0 °C

188 - 205.94 GPa

300.0 °C

164 - 198.53 GPa

400.0 °C

188.79 GPa

Poisson's ratio

20.0 °C

0.29 [-]

100.0 °C

0.29 [-]

200.0 °C

0.29 [-]

300.0 °C

0.31 [-]

400.0 °C

0.31 [-]

Reduction of area

20.0 °C

60 %

Shear modulus

20.0 °C

84.82 GPa

100.0 °C

82.5 GPa

200.0 °C

79.57 GPa

300.0 °C

75.86 GPa

400.0 °C

72 GPa

Tensile strength

20.0 °C

600 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

20.0 °C

1.02E-5 1/K

100.0 °C

1.05E-5 1/K

200.0 °C

1.09E-5 1/K

300.0 °C

1.13E-5 1/K

400.0 °C

1.16E-5 1/K

500.0 °C

1.2E-5 1/K

600.0 °C

1.22E-5 1/K

Max service temperature, long

0 - 550 °C

Melting point

1370 - 1530 °C

Typical for Martensitic Stainless Steel

Specific heat capacity

20.0 °C

439 J/(kg·K)

100.0 °C

474 J/(kg·K)

200.0 °C

498 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

538 J/(kg·K)

500.0 °C

564 J/(kg·K)

600.0 °C

598 J/(kg·K)

Thermal conductivity

20.0 °C

25.9 W/(m·K)

100.0 °C

25.3 W/(m·K)

200.0 °C

25.2 W/(m·K)

300.0 °C

25.2 W/(m·K)

400.0 °C

25.4 W/(m·K)

500.0 °C

25.7 W/(m·K)

600.0 °C

25.9 W/(m·K)

Thermal diffusivity

20.0 °C

7.6 mm²/s

100.0 °C

6.6 mm²/s

200.0 °C

6.1 mm²/s

300.0 °C

5.8 mm²/s

400.0 °C

5.3 mm²/s

500.0 °C

4.8 mm²/s

600.0 °C

4.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

5.59E-7 Ω·m

100.0 °C

6.4E-7 Ω·m

200.0 °C

7.32E-7 Ω·m

300.0 °C

8.17E-7 Ω·m

400.0 °C

8.97E-7 Ω·m

500.0 °C

9.74E-7 Ω·m

600.0 °C

1.05E-6 Ω·m

Chemical properties

PropertyValue

Carbon

0.08 - 0.12 %

Chromium

12 - 14 %

Phosphorus

0.05 %

Silicon

1 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17230 Grade 100Cr2 Steel – Annealed for Spheroidized Carbides (AC)
    2. EN 10269 Grade 21CrMoV5‑7 (Annealed + AC) – High‑Temperature Steel for Screws & Nuts
    3. DIN 1654-5 X6Cr17 Annealed for Spheroidized Carbides – Superior Cold-Forming & Corrosion Resistance
    4. DIN 1654-5 Grade X6Cr17 – Annealed for Spheroidized Carbides and Precision Turning
    5. DIN 1654-5 Grade X10Cr13: Annealed for Spheroidized Carbides and Cold-Worked Strength
    6. Optimizing DIN 17221 Grade 54SiCr6: Annealing for Spheroidized Carbides
    7. DIN 17221 Grade 55Cr3 Steel: Annealing for Spheroidized Carbides and Enhanced Performance
    8. DIN 17221 Grade 60SiCr7 – Advanced Annealing for Optimal Spheroidized Carbides
    9. DIN 17221 Grade 50CrV4: Annealed for Spheroidized Carbides (+AC) – Enhanced Performance
    10. DIN 17221 Grade 51CrMoV4 Annealed for Spheroidized Carbides (+AC) – High‑Performance Hot‑Formed Springs